The INOR-8 tube bundle of the primary heat exchanger of the Molten-Salt Reactor Experiment contains 163 1/2-in. dia. x 0.042-in.-wall U-tubes welded to a 1 1/2-in.-thick tube sheet, 17 in. in diameter. Procedures were successfully developed for welding and back brazing the closely spaced 326 tube-to-tube sheet joints in the unit. Trepan grooves were machined in the weld side of the tube sheet so that low-restraint edge-type welds could be made. The 82 Au18 Ni (wt%) brazing alloy used is corrosion resistant, ductile, and produces joints exhibiting satisfactory mechanical strength. A unique joint design incorporating a trepan groove and feeder …
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.
Description
The INOR-8 tube bundle of the primary heat exchanger of the Molten-Salt Reactor Experiment contains 163 1/2-in. dia. x 0.042-in.-wall U-tubes welded to a 1 1/2-in.-thick tube sheet, 17 in. in diameter. Procedures were successfully developed for welding and back brazing the closely spaced 326 tube-to-tube sheet joints in the unit. Trepan grooves were machined in the weld side of the tube sheet so that low-restraint edge-type welds could be made. The 82 Au18 Ni (wt%) brazing alloy used is corrosion resistant, ductile, and produces joints exhibiting satisfactory mechanical strength. A unique joint design incorporating a trepan groove and feeder holes was used for the braze side. Nondestructive inspection of the welds revealed no defects. Good general flow of the brazing alloy was evident, and ultrasonic examination of brazed joints showed only minor scattered porosity. The completed unit passed both heliumleak and 800-psi hydrostatic tests. (auth)
This report is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
Donnelly, R.G. & Slaughter, G.M.FABRICATION OF THE HEAT EXCHANGER TUBE BUNDLE FOR THE MOLTEN-SALT REACTOR EXPERIMENT,
report,
December 1, 1963;
Tennessee.
(https://digital.library.unt.edu/ark:/67531/metadc866605/:
accessed May 23, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.