From Summary: "These properties compare favorably with those of the strongest similar alloys previously investigated. However, compared with a 60Cr-25Fe-15Mo alloy, the three cobalt-chronium-nickel cast alloys are inferior. A correlation of NACA and OSRD (Project NRC-8) data is presented, showing the variation of rupture strengths with temperature in the range of 1350^o to 2000^o for alloys."
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
From Summary: "These properties compare favorably with those of the strongest similar alloys previously investigated. However, compared with a 60Cr-25Fe-15Mo alloy, the three cobalt-chronium-nickel cast alloys are inferior. A correlation of NACA and OSRD (Project NRC-8) data is presented, showing the variation of rupture strengths with temperature in the range of 1350^o to 2000^o for alloys."
This report is part of the following collections of related materials.
National Advisory Committee for Aeronautics Collection
The National Advisory Committee for Aeronautics (NACA) was a U.S. federal agency founded on March 3, 1915 to undertake, promote, and institutionalize aeronautical research. On October 1, 1958 the agency was dissolved, and its assets and personnel transferred to the newly created National Aeronautics and Space Administration (NASA).
The Technical Report Archive & Image Library (TRAIL) identifies, acquires, catalogs, digitizes and provides unrestricted access to U.S. government agency technical reports. The mission of TRAIL is to ensure preservation, discoverability, and persistent open access to government technical publications regardless of form or format.
Reynolds, E. E.; Freeman, J. W. & White, A. E.The 1350 F stress-rupture properties of two wrought alloys and three cast alloys,
report,
November 1947;
(https://digital.library.unt.edu/ark:/67531/metadc55436/:
accessed July 16, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.