This acceptance criteria is intended to prevent gross rupture or rapidly propagating failure during normal and abnormal operating conditions. Pitting may be present in the carbon steel piping. While the acceptance criteria have provisions to preclude gross rupture through a pitted region, they do not protect against throughwall pit growth and subsequent leakage. Potential leakage through a pit in low pressure piping is less than the post-DBE design basis leakage. Both the uniform thinning and LTA criteria protect against leakage, since their potential for leakage is larger. The acceptance criteria protects against gross rupture due to general wall thinning, local …
continued below
Publisher Info:
Westinghouse Savannah River Co., Aiken, SC (United States)
Place of Publication:
Aiken, South Carolina
Provided By
UNT Libraries Government Documents Department
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.
Description
This acceptance criteria is intended to prevent gross rupture or rapidly propagating failure during normal and abnormal operating conditions. Pitting may be present in the carbon steel piping. While the acceptance criteria have provisions to preclude gross rupture through a pitted region, they do not protect against throughwall pit growth and subsequent leakage. Potential leakage through a pit in low pressure piping is less than the post-DBE design basis leakage. Both the uniform thinning and LTA criteria protect against leakage, since their potential for leakage is larger. The acceptance criteria protects against gross rupture due to general wall thinning, local wall thinning (LTA's), pitting, and fracture through weld defects. General wall thinning calculations are based on the restart criteria, SEP-24. LTA criteria for hoop stresses are based on ASME Code Case N-480 [open quotes]Examination Requirements for Pipe Wall Thinning Due to Single Phase Erosion and Corrosion[close quotes]. The LTA criteria for axial stress is based on an effective average thickness concept, which prevents plastic collapse of a locally thinned pipe. Limits on pit density, based on an effective cross section concept, are used to prevent gross rupture through a group of pits. The CEGB R-6 failure assessment diagram is used in the fracture evaluation, along with postulated weld defects. This criteria is intended for low temperature, low pressure piping systems. Corrosion and/or weld defects increase the peak stresses during normal operation and may lead to a reduction in fatigue life. Piping systems subject to significant thermal or mechanical fatigue will require additional analysis which is beyond the scope of this document.
This report is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
Mertz, G. E.Wall thinning criteria for low temperature-low pressure piping,
report,
January 1, 1993;
Aiken, South Carolina.
(https://digital.library.unt.edu/ark:/67531/metadc1187295/:
accessed May 27, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.