The influence of uniaxial compression upon the Hall effect ad resistivity of cadmium-doped samples of InSb at 77 K, 64 K, and 12 K are reported. Unilaxial compressions as high as 6 kbar were applied to samples oriented in the {001} and {110} directions. The net hole concentration of the samples were about 5x10^13 cm^-3 at 77 K as determined from the Hall coefficient at 24 kilogauss. The net concentration of hole carriers decreases and then increases exponentially with stress at 77 k and 64 k, while at 12 k there is only a monotonic increase of carrier concentration with …
continued below
The UNT Libraries serve the university and community by providing access to physical and online collections, fostering information literacy, supporting academic research, and much, much more.
The influence of uniaxial compression upon the Hall effect ad resistivity of cadmium-doped samples of InSb at 77 K, 64 K, and 12 K are reported. Unilaxial compressions as high as 6 kbar were applied to samples oriented in the {001} and {110} directions. The net hole concentration of the samples were about 5x10^13 cm^-3 at 77 K as determined from the Hall coefficient at 24 kilogauss. The net concentration of hole carriers decreases and then increases exponentially with stress at 77 k and 64 k, while at 12 k there is only a monotonic increase of carrier concentration with stress. Analysis of the hole concentration as a function of stress shows the presence of a deep acceptor level located about 90 meV above the valence band edge in additionb to the 10 meV vadmium acceptor level. The shallow acceptor level does not split with stress. The hole density data is represented very well by models which describe both the variation in the net density of states and motion of the acceptor levels as a function of stress.
This dissertation is part of the following collection of related materials.
UNT Theses and Dissertations
Theses and dissertations represent a wealth of scholarly and artistic content created by masters and doctoral students in the degree-seeking process. Some ETDs in this collection are restricted to use by the UNT community.