SRNL was requested by WSRC Waste Solidification Engineering to characterize the release of ammonia from saltstone curing at 95 C by performing experimental testing. These tests were performed with an MCU-type Tank 50H salt simulant containing 0, 50, and 200 mg/L ammonia. The testing program showed that above saltstone made from the 200 mg/L ammonia simulant, the vapor space ammonia concentration was about 2.7 mg/L vapor at 95 C. An upper 95% confidence value for this concentration was found to be 3.9 mg/L. Testing also showed that ammonia was chemically generated from curing saltstone at 95 C; the amount of …
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.
Description
SRNL was requested by WSRC Waste Solidification Engineering to characterize the release of ammonia from saltstone curing at 95 C by performing experimental testing. These tests were performed with an MCU-type Tank 50H salt simulant containing 0, 50, and 200 mg/L ammonia. The testing program showed that above saltstone made from the 200 mg/L ammonia simulant, the vapor space ammonia concentration was about 2.7 mg/L vapor at 95 C. An upper 95% confidence value for this concentration was found to be 3.9 mg/L. Testing also showed that ammonia was chemically generated from curing saltstone at 95 C; the amount of ammonia generated was estimated to be equivalent to 121 mg/L additional ammonia in the salt solution feed. Even with chemical generation, the ammonia release from saltstone was found to be lower than its release from salt solution only with 200 mg/L ammonia.
This report is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
Zamecnik, J & Alex Cozzi, A.MEASUREMENT OF AMMONIA RELEASE FROM SALTSTONE,
report,
January 15, 2009;
South Carolina.
(https://digital.library.unt.edu/ark:/67531/metadc925771/:
accessed July 17, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.