Theoretical predictions of thin-film CdS/CdTe photovoltaic (PV) devices have suggested performance may be improved by reducing recombination due to Te-vacancy (VTe) or Te-interstitial (Tei) defects. Although formation of these intrinsic defects is likely influenced by CdTe deposition parameters, it also may be coupled to formation of beneficial cadmium vacancy (VCd) defects. If this is true, reducing potential effects of VTe or Tei may be difficult without also reducing the density of VCd. In contrast, post-deposition processes can sometimes afford a greater degree of defect control. Here we explore a post-deposition process that appears to influence the Te-related defects in polycrystalline …
continued below
Publisher Info:
National Renewable Energy Laboratory (NREL), Golden, CO.
Place of Publication:
Golden, Colorado
Provided By
UNT Libraries Government Documents Department
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this article.
Follow the links below to find similar items on the Digital Library.
Description
Theoretical predictions of thin-film CdS/CdTe photovoltaic (PV) devices have suggested performance may be improved by reducing recombination due to Te-vacancy (VTe) or Te-interstitial (Tei) defects. Although formation of these intrinsic defects is likely influenced by CdTe deposition parameters, it also may be coupled to formation of beneficial cadmium vacancy (VCd) defects. If this is true, reducing potential effects of VTe or Tei may be difficult without also reducing the density of VCd. In contrast, post-deposition processes can sometimes afford a greater degree of defect control. Here we explore a post-deposition process that appears to influence the Te-related defects in polycrystalline CdTe. Specifically, we have exposed the CdTe surface to Te prior to ZnTe:Cu/Ti contact-interface formation with the goal of reducing VTe but without significantly reducing VCd. Initial results show that when this modified contact is used on a CdCl2-treated CdS/CdTe device, significantly poorer device performance results. This suggests two things: First, the amount of free-Te available during contact formation (either from chemical etching or CuTe or ZnTe deposition) may be a more important parameter to device performance than previously appreciated. Second, if processes have been used to reduce the effect of VTe (e.g., oxygen and chlorine additions to the CdTe), adding even a small amount of Te may produce detrimental defects.
This article is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
Gessert, T. A.; Burst, J. M.; Ma, J.; Wei, S. H.; Kuciauskas, D.; Barnes, T. M. et al.Response of Cds/CdTe Devices to Te Exposure of Back Contact: Preprint,
article,
June 1, 2012;
Golden, Colorado.
(https://digital.library.unt.edu/ark:/67531/metadc829032/:
accessed July 16, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.