Fracture Toughness of 6.4 Mm (0.25 Inch) Arc-Cast Molobdenum and Molybdenum-Tzm Plate at Room Temperature and 300 Degrees C

Thumbnail image of item number 1 in: 'Fracture Toughness of 6.4 Mm (0.25 Inch) Arc-Cast Molobdenum and Molybdenum-Tzm Plate at Room Temperature and 300 Degrees C'.
Thumbnail image of item number 2 in: 'Fracture Toughness of 6.4 Mm (0.25 Inch) Arc-Cast Molobdenum and Molybdenum-Tzm Plate at Room Temperature and 300 Degrees C'.
Thumbnail image of item number 3 in: 'Fracture Toughness of 6.4 Mm (0.25 Inch) Arc-Cast Molobdenum and Molybdenum-Tzm Plate at Room Temperature and 300 Degrees C'.
Thumbnail image of item number 4 in: 'Fracture Toughness of 6.4 Mm (0.25 Inch) Arc-Cast Molobdenum and Molybdenum-Tzm Plate at Room Temperature and 300 Degrees C'.
Showing 1-4 of 11 pages in this article.

PDF Version Also Available for Download.

Description

THE FRACTURE TOUGHNESS OF 6.4 mm (0.25 INCH) LOW CARBON ARC-CAST (LCAC) MOLYBDENUM AND ARC-CAST MOLYBDENUM-TZM ALLOY PLATE WERE MEASURED AT ROOM TEMPERATURE AND 300 DEGREES C USING COMPACT TNESION SPECIMENTS. THE EFFECT OF CRACK PLANE ORIENTATION (LONGITUDINAL VS. TRANSVERSE) AND ANNEALING PRACTICE (STRESS-RELIEVED VS. RECRYSTALLIZED) WERE EVALUATED. DEPENDING UPON THE TEST TEMPERATURE EITHER A STANDARD K[SUB]IC OR A J-INTEGRAL ANALYSIS WAS USED TO OBTAIN THE TOUGHNESS VALUE. AT ROOM TEMPERATURE, REGARDLESS OF ALLOY, ORIENTATION, OR MICROSTURECTURE, FRACTURE TOUGHNESS VALUES BETWEEN 15 AND 22 MPa m{sup 1/2} (14 AND 20 KSI IN{sup 1/2}) WERE MEASURED. THESE K[SUB]IC VALUES WERE CONSISTENT … continued below

Physical Description

vp.

Creation Information

Shields, J. A., Jr.; Lipetzky, P. & Mueller, A. J. April 11, 2001.

Context

This article is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by the UNT Libraries Government Documents Department to the UNT Digital Library, a digital repository hosted by the UNT Libraries. It has been viewed 99 times. More information about this article can be viewed below.

Who

People and organizations associated with either the creation of this article or its content.

Authors

Sponsor

Publisher

  • Bettis Atomic Power Laboratory
    Publisher Info: Bettis Atomic Power Lab., West Mifflin, PA (United States)
    Place of Publication: West Mifflin, Pennsylvania

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

About | Browse this Partner

Contact Us

Corrections Questions

What

Descriptive information to help identify this article. Follow the links below to find similar items on the Digital Library.

Description

THE FRACTURE TOUGHNESS OF 6.4 mm (0.25 INCH) LOW CARBON ARC-CAST (LCAC) MOLYBDENUM AND ARC-CAST MOLYBDENUM-TZM ALLOY PLATE WERE MEASURED AT ROOM TEMPERATURE AND 300 DEGREES C USING COMPACT TNESION SPECIMENTS. THE EFFECT OF CRACK PLANE ORIENTATION (LONGITUDINAL VS. TRANSVERSE) AND ANNEALING PRACTICE (STRESS-RELIEVED VS. RECRYSTALLIZED) WERE EVALUATED. DEPENDING UPON THE TEST TEMPERATURE EITHER A STANDARD K[SUB]IC OR A J-INTEGRAL ANALYSIS WAS USED TO OBTAIN THE TOUGHNESS VALUE. AT ROOM TEMPERATURE, REGARDLESS OF ALLOY, ORIENTATION, OR MICROSTURECTURE, FRACTURE TOUGHNESS VALUES BETWEEN 15 AND 22 MPa m{sup 1/2} (14 AND 20 KSI IN{sup 1/2}) WERE MEASURED. THESE K[SUB]IC VALUES WERE CONSISTENT WITH MEASUREMENTS BY THE AUTHORS. INCREASING TEMPERATURE IMPROVES THE TOUGHNESS, DUE TO THE FACT THAT ONE TAKES ADVANTAGE OF THE DUCTIVE-BRITTLE TRANSITION BEHAVIOR OF MOLYBDENUM. AT 300 DEGREES C, THE FRACTURE TOUGHNESS OF RECRYSTALLIZED LCAC AND ARC-CAST TZM MOLYBDENUM WERE ALSO SIMILAR AT APPROXI MATELY 64 MPa m{sup 1/2} (58 KSI IN{sup 1/2}). IN THE STRESS-RELIEVED CONDITION, HOWEVER, THE TOUGHNESS OF ARC-CAST TZM (91 MPa m{sup 1/2}/83 KSI IN{sup 1/2}) WAS HIGHER THAN THAT OF THE LCAC MOLYBDENUM (74 MPa m{sup 1/2}/67 KSI IN{sup 1/2}).

Physical Description

vp.

Notes

OSTI as DE00793544

Source

  • 15th International Plansee Seminar, Reutte (AT), 05/28/2001

Language

Item Type

Identifier

Unique identifying numbers for this article in the Digital Library or other systems.

  • Report No.: B-T-3326
  • Grant Number: AC11-98PN38206
  • Office of Scientific & Technical Information Report Number: 793544
  • Archival Resource Key: ark:/67531/metadc743116

Collections

This article is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

About | Browse this Collection

What responsibilities do I have when using this article?

Digital Files

When

Dates and time periods associated with this article.

Creation Date

  • April 11, 2001

Added to The UNT Digital Library

  • Oct. 19, 2015, 7:39 p.m.

Description Last Updated

  • Jan. 21, 2024, 2:40 p.m.

Usage Statistics

When was this article last used?

Yesterday: 0
Past 30 days: 0
Total Uses: 99
More Statistics

Interact With This Article

Here are some suggestions for what to do next.

Start Reading

Thumbnail image of item number 1 in: 'Fracture Toughness of 6.4 Mm (0.25 Inch) Arc-Cast Molobdenum and Molybdenum-Tzm Plate at Room Temperature and 300 Degrees C'.
Thumbnail image of item number 2 in: 'Fracture Toughness of 6.4 Mm (0.25 Inch) Arc-Cast Molobdenum and Molybdenum-Tzm Plate at Room Temperature and 300 Degrees C'.
Thumbnail image of item number 3 in: 'Fracture Toughness of 6.4 Mm (0.25 Inch) Arc-Cast Molobdenum and Molybdenum-Tzm Plate at Room Temperature and 300 Degrees C'.
Thumbnail image of item number 4 in: 'Fracture Toughness of 6.4 Mm (0.25 Inch) Arc-Cast Molobdenum and Molybdenum-Tzm Plate at Room Temperature and 300 Degrees C'.

PDF Version Also Available for Download.

Citations, Rights, Re-Use

International Image Interoperability Framework

IIF Logo

We support the IIIF Presentation API

Links for Robots

Helpful links in machine-readable formats.

Archival Resource Key (ARK)

International Image Interoperability Framework (IIIF)

Metadata Formats

Images

URLs

Stats

Shields, J. A., Jr.; Lipetzky, P. & Mueller, A. J. Fracture Toughness of 6.4 Mm (0.25 Inch) Arc-Cast Molobdenum and Molybdenum-Tzm Plate at Room Temperature and 300 Degrees C, article, April 11, 2001; West Mifflin, Pennsylvania. (https://digital.library.unt.edu/ark:/67531/metadc743116/: accessed July 16, 2024), University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu; crediting UNT Libraries Government Documents Department.

Back to Top of Screen