Abstract: "The oxidation resistance of thin sheets of iron-28 w/o chromium-2.67 to 10.0 w/o alloys, nominally 0.004, 0.006, 0.008, 0.012, and 0.016 in. thick, was determined by exposure in static air for 100 hr at 2100 and 2300 F. A minimum of 3.67 and 9.37 w/o aluminum was necessary to prevent excessive oxidation of 0.004-in.-thick sheet material at 2100 and 2300 F, respectively. Correspondingly, specimens of lower aluminum content and greater thickness withstood the oxidation attack. Oxidation of iron-chromium-aluminum alloys appeared to be related to the diffusion of aluminum to surfaces of the sheet to form an adherent protective layer …
continued below
We've identified this
report
as a primary source within our collections. Researchers, educators, and students may find this report useful in their work.
Provided By
UNT Libraries Government Documents Department
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Added Title:
Battelle Memorial Institute ReportBMI-1230
Description
Abstract: "The oxidation resistance of thin sheets of iron-28 w/o chromium-2.67 to 10.0 w/o alloys, nominally 0.004, 0.006, 0.008, 0.012, and 0.016 in. thick, was determined by exposure in static air for 100 hr at 2100 and 2300 F. A minimum of 3.67 and 9.37 w/o aluminum was necessary to prevent excessive oxidation of 0.004-in.-thick sheet material at 2100 and 2300 F, respectively. Correspondingly, specimens of lower aluminum content and greater thickness withstood the oxidation attack. Oxidation of iron-chromium-aluminum alloys appeared to be related to the diffusion of aluminum to surfaces of the sheet to form an adherent protective layer of Al2O3."
This report is part of the following collections of related materials.
Technical Report Archive and Image Library
The Technical Report Archive & Image Library (TRAIL) identifies, acquires, catalogs, digitizes and provides unrestricted access to U.S. government agency technical reports. The mission of TRAIL is to ensure preservation, discoverability, and persistent open access to government technical publications regardless of form or format.
Imaged from microcard, these technical reports describe research performed for U.S. government agencies from the 1930s to the 1960s. The reports were provided by the Technical Report Archive and Image Library (TRAIL).
Jablonowski, Edward J.; Shober, Frederic R. & Dickerson, Ronald F.High-Temperature Oxidation Resistance of Thin Iron-Chromium-Aluminum Alloy Sheet,
report,
October 22, 1957;
Columbus, Ohio.
(https://digital.library.unt.edu/ark:/67531/metadc714192/:
accessed June 22, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.