The effect of temperature on the yield strength of the polycrystalline hexagonal Ag-Al intermetallic phase was investigated over the temperature range 77 to 775 K. It was found that the curve for yield stress vs temperature for both polycrystalline Ag-33 at .% Al specimens that were heavily cold worked prior to deformation and those that were recrystallized prior to deformation was parallel to that for prismatic slip in single crystals.
We've identified this
report
as a primary source within our collections. Researchers, educators, and students may find this report useful in their work.
Provided By
UNT Libraries Government Documents Department
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Added Title:
University of California Radiation Laboratory Report UCRL-9992
Description
The effect of temperature on the yield strength of the polycrystalline hexagonal Ag-Al intermetallic phase was investigated over the temperature range 77 to 775 K. It was found that the curve for yield stress vs temperature for both polycrystalline Ag-33 at .% Al specimens that were heavily cold worked prior to deformation and those that were recrystallized prior to deformation was parallel to that for prismatic slip in single crystals.
This report is part of the following collections of related materials.
TRAIL Microcard Collection
Imaged from microcard, these technical reports describe research performed for U.S. government agencies from the 1930s to the 1960s. The reports were provided by the Technical Report Archive and Image Library (TRAIL).
The Technical Report Archive & Image Library (TRAIL) identifies, acquires, catalogs, digitizes and provides unrestricted access to U.S. government agency technical reports. The mission of TRAIL is to ensure preservation, discoverability, and persistent open access to government technical publications regardless of form or format.
Tanaka, Kichinosuko & Mote, Jim D.The Effect of Temperature on the Yield Strength of the Polycrystalline Hexagonal Ag-Al Intermetallic Phase,
report,
December 18, 1961;
Livermore, California.
(https://digital.library.unt.edu/ark:/67531/metadc1255495/:
accessed July 18, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.