An experiment was conducted at LLL that required low-density, fine-celled foams uniformly loaded with rubidium. Foams meeting these requirements were produced by impregnating foams made from polyacrylonitrile with rubidium fluoride. Foams with densities from 0.025 to 0.4 g/cm/sup 3/ were prepared and loaded with 0.002 to 0.20 g/cm/sup 3/ of rubidium fluoride.
Publisher Info:
California Univ., Livermore (USA). Lawrence Livermore Lab.
Place of Publication:
Livermore, California
Provided By
UNT Libraries Government Documents Department
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.
Description
An experiment was conducted at LLL that required low-density, fine-celled foams uniformly loaded with rubidium. Foams meeting these requirements were produced by impregnating foams made from polyacrylonitrile with rubidium fluoride. Foams with densities from 0.025 to 0.4 g/cm/sup 3/ were prepared and loaded with 0.002 to 0.20 g/cm/sup 3/ of rubidium fluoride.
This report is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.