A detailed economic evaluation is presented of several EFG ribbon growth technology scenarios using the ''SAMICS'' interim price estimation guidelines. It is concluded that the growth of 10 ribbons from a double five ribbon furnace of the general type represented by the existing Machine 3A would meet the requirements of producing ribbon at a price below $20/m/sup 2/ the 1986 goal. The technology requirements are that one operator can operate 2 of the 5 ribbon growth stations in which each ribbon grows at a speed of 7.5 cm/min and is also 7.5 cm wide. The machines also would have to …
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.
Description
A detailed economic evaluation is presented of several EFG ribbon growth technology scenarios using the ''SAMICS'' interim price estimation guidelines. It is concluded that the growth of 10 ribbons from a double five ribbon furnace of the general type represented by the existing Machine 3A would meet the requirements of producing ribbon at a price below $20/m/sup 2/ the 1986 goal. The technology requirements are that one operator can operate 2 of the 5 ribbon growth stations in which each ribbon grows at a speed of 7.5 cm/min and is also 7.5 cm wide. The machines also would have to achieve a duty cycle of 67% at minimum and yields above 75%. Finally, silicon must be available at $10 to approximately $25/kg, depending on the yield assumed. These conclusions are the final results of the economic analysis. The progress towards the growth of 7.5 cm wide ribbon at 7.5 cm/min is discussed. Also, fluid flow phenomena have been investigated and it is shown that by utilization of such phenomena the impurity distribution in the ribbon may be manipulated to a significant extent. Also, using a somewhat novel ''EBIC'' technique it was demonstrated that the internal grain structure found previously in some ribbons grown at high speeds has virtually no influence on the performance of the material when made into a solar cell.
This report is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
Wald, F.V.Large area silicon sheet by EFG. Fourth quarterly report, October 1, 1977--December 31, 1977,
report,
January 15, 1978;
United States.
(https://digital.library.unt.edu/ark:/67531/metadc1194216/:
accessed July 4, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.