Information concerning the dimensionality of the superconductive fluctuations in the new high temperature superconductors can be derived from the excess conductivity (or paraconductivity) near the transition temperature. Here the lowering'' of the sample resistance in the same temperature regions is used for extraction of dimensionality and generally for comparative studies of the critical behaviour of three different samples such as YBa{sub 2}Cu{sub 3}O{sub 7}, Y{sub 0.8}Gd{sub 0.2}Ba{sub 2}Cu{sub 3}O{sub 7} and Bi{sub 0. 85}Pb{sub 0.15}SrCa{sub 1.2}Cu{sub 2}O{sub 6}. The experimental data of the three samples show a similar behaviour with some distinct differences depending rather on the metallurgical'' state of …
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this article.
Follow the links below to find similar items on the Digital Library.
Description
Information concerning the dimensionality of the superconductive fluctuations in the new high temperature superconductors can be derived from the excess conductivity (or paraconductivity) near the transition temperature. Here the lowering'' of the sample resistance in the same temperature regions is used for extraction of dimensionality and generally for comparative studies of the critical behaviour of three different samples such as YBa{sub 2}Cu{sub 3}O{sub 7}, Y{sub 0.8}Gd{sub 0.2}Ba{sub 2}Cu{sub 3}O{sub 7} and Bi{sub 0. 85}Pb{sub 0.15}SrCa{sub 1.2}Cu{sub 2}O{sub 6}. The experimental data of the three samples show a similar behaviour with some distinct differences depending rather on the metallurgical'' state of the material than the composition itself. A logarithmic behaviour is present for YBaCuO and Y(Gd)BaCuO samples not close to the critical temperature and, the most important, closer to {Tc} YBaCuO shows a fractal behaviour, observed for the first time, similar to the one of Bi-compound observed many times before.
This article is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
Patapis, S. K.; Sideridis, L.; Apostolopoulos, G.; Ausloos, M.; Luo, H. L.; Politis, C. (Kernforschungszentrum Karlsruhe GmbH (Germany). Inst. fuer Nukleare Festkoerperphysik) et al.Paraconductivity measurements and comparative studies of fluctuations in BiSrCaCuO, YBaCuO and YBaCuO with Gd substitution,
article,
January 1, 1991;
Illinois.
(https://digital.library.unt.edu/ark:/67531/metadc1102302/:
accessed July 16, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.