Experiments were performed using a thermogravimetric analysis (TGA) system by Pacific Northwest National Laboratory (PNNL)to study the drying behavior of the K-Basin spent nuclear fuel (SNF) internal sludge and two different surface coatings of SNF elements. These measurements were conducted in support of the safety and process analyses of the proposed Integrated Process Strategy (IPS) to move the N-Reactor fuel stored at K-Basin to an interim storage facility. These limited experiments on the corrosion products of K-Basin SNF material were part of the broad studies performed to ascertain the bounding pressurization of the Multi-Canister Overpack (MCO). Seven SNF internal sludge …
continued below
Publisher Info:
Pacific Northwest National Lab., Richland, WA (United States)
Place of Publication:
Richland, Washington
Provided By
UNT Libraries Government Documents Department
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.
Description
Experiments were performed using a thermogravimetric analysis (TGA) system by Pacific Northwest National Laboratory (PNNL)to study the drying behavior of the K-Basin spent nuclear fuel (SNF) internal sludge and two different surface coatings of SNF elements. These measurements were conducted in support of the safety and process analyses of the proposed Integrated Process Strategy (IPS) to move the N-Reactor fuel stored at K-Basin to an interim storage facility. These limited experiments on the corrosion products of K-Basin SNF material were part of the broad studies performed to ascertain the bounding pressurization of the Multi-Canister Overpack (MCO). Seven SNF internal sludge samples taken from different damage regions of three damaged/corroded outer K-Basin SNF elements were dried. Additionally, two surface coating samples taken from two SNF elements stored at K-West were tested. All the tests were performed in a vacuum atmosphere with the same temperature ramp rate of about 0.4 C/ min. Each TGA test sample was weighed before and after the test on a balance located in the Shielded Analytical Laboratory hot cell. The test samples were vacuum dried in the TGA system for about 24 hours prior to heating them at the rate of 0.4 C/min. The observations from the weight change data are summarized below.
This report is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
Abrefah, J.; Alexander, D. L. & Marschman, S. C.Drying Results of K-Basin Damaged/Corroded SNF Internal Sludge and Surface Coating,
report,
September 21, 2000;
Richland, Washington.
(https://digital.library.unt.edu/ark:/67531/metadc720872/:
accessed May 2, 2024),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.