Porosity in as-cast U-Al alloy
Description:
This memorandum documents a study that showed a cyclic occurrence of porosity in U-Al alloys produced in Building 321-M. Review of process data shows that the extent of porosity is more pronounced in months of warm, humid weather and less pronounced in cooler, drier months. This porosity is most likely caused by hydrogen, which becomes dissolved in the molten U-Al alloy during casting. Although excessive porosity was the cause of some observed process anomalies, this type of porosity has no sig…