Influence of ordered L1₂ precipitation on strain-rate dependent mechanical behavior in a eutectic high entropy alloy
Description:
This article focuses on Al0.7CoCrFeNi, a lamellar dual-phase (fcc + B2) precipitation-strengthenable eutectic high entropy alloy. The back-stresses from the coherent L12 precipitate were insufficient to cause improvement in twin nucleation, owing to elevated twinning stress under quasi-static testing. However, under dynamic testing high density of twins were observed.
Date:
April 23, 2019
Creator:
Gwalani, Bharat; Gangireddy, Sindhura; Zheng, Yufeng; Soni, V.; Mishra, Rajiv & Banerjee, Rajarshi