Mechanical properties of oxide dispersion strengthened (ODS) molybdenum alloys

Description: Oxide dispersion strengthened molybdenum, Mo-ODS, developed by a proprietary powder metallurgy process, exhibits a creep rupture life at 0.65T{sub m} (1,600 C) of three to five orders of magnitude greater than unalloyed molybdenum, while maintaining ductile fracture behavior at temperatures significantly below room temperature. In comparison, the creep rupture life of the Mo-50Re solid solution strengthened alloy at 1,600 C is only an order of magnitude greater than unalloyed molybdenum. The results of microstructural characterization and thermal stability and mechanical property testing are discussed.
Date: March 1, 1998
Creator: Bianco, R. & Buckman, R.W. Jr.
Partner: UNT Libraries Government Documents Department

Evaluation of Oxide Dispersion Strengthened (ODS) molybdenum alloys

Description: A series of fourteen (14) novel high-strength molybdenum alloy compositions containing a dispersion of very fine (< 1 {mu}m diameter) oxide particles were consolidated using two proprietary powder metallurgy techniques. The developmental compositions were evaluated to determine the microstructural stability and mechanical properties from cryogenic (-148{degrees}F) to elevated temperatures (4000{degrees}F) for material in the as-swaged (>98% cold work) condition and for as-swaged material in the heat treated condition. Extremely fine oxide particle sizes (<1000 {Angstrom}) were observed by Transmission Electron Microscopy (TEM) for a number of the experimental compositions in the as-swaged condition. A one hour recrystallization temperature as high as 3990{degrees}F was measured and a ductile-to-brittle transition temperature as low as {approximately}58{degrees}F for material in the recrystallized condition was determined. The preliminary results support the alloy design concept feasibility.
Date: December 31, 1995
Creator: Bianco, R. & Buckman, R.W. Jr.
Partner: UNT Libraries Government Documents Department

Evaluation of oxide dispersion strengthened (ODS) molybdenum and molybdenum-rhenium Alloys

Description: Oxide dispersion strengthened (ODS) molybdenum alloys being developed for high temperature applications possess excellent high temperature strength and creep resistance. In addition they exhibit a ductile-to-brittle transition temperature (DBIT) in the worked and stress-relieved condition under longitudinal tensile load well below room temperature. However, in the recrystallized condition, the DBTT maybe near or above room temperature, depending on the volume fraction of oxide dispersion and the amount of prior work. Dilute rhenium additions (7 and 14 wt.%) to ODS molybdenum were evaluated to determine their effect on low temperature ductility. The addition of 7 wt.% rhenium to the ODS molybdenum did not significantly enhance the mechanical properties. However, the addition of 14 wt.% rhenium to the ODS molybdenum resulted in a DBTT well below room temperature in both the stress-relieved and recrystallized condition. Additionally, the tensile strength of ODS Mo-14Re is greater than the base ODS molybdenum at 1,000 to 1,250 C.
Date: October 22, 1999
Creator: Mueller, A.J.; Bianco, R. & Buckman, R.W. Jr.
Partner: UNT Libraries Government Documents Department