Description: The focus of the following research was to (1) understand the chemistry involved in nitriding an organosilicate glass substrate prior to tantalum deposition, as well as the effect nitrogen incorporation plays on subsequent tantalum deposition and (2) the reduction of a native oxide, the removal of surface contaminants, and the etching of a HgCdTe surface utilizing atomic hydrogen. These studies were investigated utilizing XPS, TEM and AFM. XPS data show that bombardment of an OSG substrate with NH3 and Ar ions results in the removal of carbon species and the incorporation of nitrogen into the surface. Tantalum deposition onto a nitrided OSG surface results in the initial formation of tantalum nitride with continued deposition resulting in the formation of tantalum. This process is a direct method for forming a thin TaN/Ta bilayer for use in micro- and nanoelectronic devices. Exposure to atomic hydrogen is shown to increase the surface roughness of both air exposed and etched samples. XPS results indicate that atomic hydrogen reduces tellurium oxide observed on air exposed samples via first-order kinetics. The removal of surface contaminants is an important step prior to continued device fabrication for optimum device performance. It is shown here that atomic hydrogen effectively removes adsorbed chlorine from the HgCdTe surface.
Date: August 2010
Creator: Wilks, Justin
Item Type: Thesis or Dissertation
Partner: UNT Libraries