Dependence of Gas-Phase Crotonaldehyde Hydrogenation Selectivity and Activity on the Size of Pt Nanoparticles (1.7-7.1 nm) Supported on SBA-15

PDF Version Also Available for Download.

Description

The selectivity and activity for the hydrogenation of crotonaldehyde to crotyl alcohol and butyraldehyde was studied over a series of Pt nanoparticles (diameter of 1.7, 2.9, 3.6, and 7.1 nm). The nanoparticles were synthesized by the reduction of chloroplatinic acid by alcohol in the presence of poly(vinylpyrrolidone) (PVP), followed by encapsulation into mesoporous SBA-15 silica. The rate of crotonaldehyde hydrogenation and selectivity towards crotyl alcohol both increase with increasing particle size. The selectivity towards crotyl alcohol increased from 13.7 % to 33.9 % (8 Torr crotonaldehyde, 160 Torr H{sub 2} and 353 K), while the turnover frequency increases from 2.1 ... continued below

Creation Information

Grass, Michael; Rioux, Robert & Somorjai, Gabor A. August 3, 2008.

Context

This article is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. More information about this article can be viewed below.

Who

People and organizations associated with either the creation of this article or its content.

Publisher

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this article. Follow the links below to find similar items on the Digital Library.

Description

The selectivity and activity for the hydrogenation of crotonaldehyde to crotyl alcohol and butyraldehyde was studied over a series of Pt nanoparticles (diameter of 1.7, 2.9, 3.6, and 7.1 nm). The nanoparticles were synthesized by the reduction of chloroplatinic acid by alcohol in the presence of poly(vinylpyrrolidone) (PVP), followed by encapsulation into mesoporous SBA-15 silica. The rate of crotonaldehyde hydrogenation and selectivity towards crotyl alcohol both increase with increasing particle size. The selectivity towards crotyl alcohol increased from 13.7 % to 33.9 % (8 Torr crotonaldehyde, 160 Torr H{sub 2} and 353 K), while the turnover frequency increases from 2.1 x 10{sup -2} s{sup -1} to 4.8 x 10{sup -2} s{sup -1} with an increase in the particle size from 1.7 nm to 7.1 nm. The decarbonylation pathway to form propene and CO is enhanced over the higher proportion of coordinatively unsaturated sites on the smaller nanoparticles. The apparent activation energy remains constant ({approx} 16 kcal mol{sup -1} for the formation of butyraldehyde and {approx} 8 kcal mol{sup -1} for the formation of crotyl alcohol) as a function of particle size. In the presence of 130-260 mTorr CO, the reaction rate decreases for all products with a CO reaction order of -0.9 for crotyl alcohol and butyraldehyde over 7.1 nm Pt particles; over 1.7 nm Pt particles, the order in CO is -1.4 and -0.9, respectively. Hydrogen reduction at 673 K after calcination in oxygen results in increased activity and selectivity relative to reduction at either higher or lower temperature; this is discussed with regards to the incomplete removal and/or change in morphology of the polymeric surface stabilizing agent, poly(vinylpyrrolidone) used for the synthesis of the Pt nanoparticles.

Source

  • Journal Name: Catalysis Letters

Language

Item Type

Identifier

Unique identifying numbers for this article in the Digital Library or other systems.

  • Report No.: LBNL-2434E
  • Grant Number: DE-AC02-05CH11231
  • Office of Scientific & Technical Information Report Number: 972040
  • Archival Resource Key: ark:/67531/metadc933630

Collections

This article is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this article?

When

Dates and time periods associated with this article.

Creation Date

  • August 3, 2008

Added to The UNT Digital Library

  • Nov. 13, 2016, 7:26 p.m.

Description Last Updated

  • Nov. 18, 2016, 2:29 p.m.

Usage Statistics

When was this article last used?

Yesterday: 0
Past 30 days: 2
Total Uses: 5

Interact With This Article

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

International Image Interoperability Framework

IIF Logo

We support the IIIF Presentation API

Grass, Michael; Rioux, Robert & Somorjai, Gabor A. Dependence of Gas-Phase Crotonaldehyde Hydrogenation Selectivity and Activity on the Size of Pt Nanoparticles (1.7-7.1 nm) Supported on SBA-15, article, August 3, 2008; Berkeley, California. (digital.library.unt.edu/ark:/67531/metadc933630/: accessed October 17, 2018), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.