Effect of Key Parameters on the Photocatalytic Oxidation of Toluene at Low Concentrations in Air under 254 + 185 nm UV Irradiation

PDF Version Also Available for Download.

Description

The effect of key experimental parameters on the removal of toluene under 254 + 185 nm irradiation was investigated using a benchtop photocatalytic flow reactor. Toluenewas introduced at low concentrations between 10 and 500 ppbv, typical of indoorenvironments, and reacted on TiO2-coated Raschig rings. Two different TiO2-coated rings were prepared: in one case, by dip-coating using a P25 aqueous suspension and, on the other, using an organic/inorganic sol-gel method that produced thin films of mesoporous anatase. Flow rates in the photoreactor varied between 4 L min-1 and 125 mL min-1, leading to residence times in the range 100 ms< tau< ... continued below

Creation Information

Quici, Natalia; Vera, Maria L.; Choi, Hyeok; Puma, Gianluca Li; Dionysiou, Dionysios D.; Litter, Marta I. et al. July 1, 2009.

Context

This article is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. It has been viewed 26 times , with 5 in the last month . More information about this article can be viewed below.

Who

People and organizations associated with either the creation of this article or its content.

Publisher

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this article. Follow the links below to find similar items on the Digital Library.

Description

The effect of key experimental parameters on the removal of toluene under 254 + 185 nm irradiation was investigated using a benchtop photocatalytic flow reactor. Toluenewas introduced at low concentrations between 10 and 500 ppbv, typical of indoorenvironments, and reacted on TiO2-coated Raschig rings. Two different TiO2-coated rings were prepared: in one case, by dip-coating using a P25 aqueous suspension and, on the other, using an organic/inorganic sol-gel method that produced thin films of mesoporous anatase. Flow rates in the photoreactor varied between 4 L min-1 and 125 mL min-1, leading to residence times in the range 100 ms< tau< 2 s. For these conditions, toluene removal efficiencies were between 30 and 90percent, indicating that the system did not achieve total conversion in any case. For each air flow rate, the conversion oftoluene was significantly higher when the reactor length was 10 cm, as compared with 5 cm; however, only marginal increases in conversions were achieved in the two reactor lengths at equal residence time and different concentration of toluene, suggesting that that the reactor is effectively behaving as an ideal reactor and that the reaction is first-order in the concentration of toluene. Experiments were carried out between 0 and 66percent relative humidity (RH), the fastest reaction rate being observed at moderately low humidity conditions (10percent RH), with respect to both dry air and higher humidity levels. Formaldehyde was formed as a partial oxidation byproduct at low and at high residence times (240 and 960 ms), although higher formaldehyde molar yields (up to 20percent) were observed at low tau (240 ms) and moderate humidity conditions (10 and 33percent), suggesting that both tau and RH can be optimized toreduce the formation of harmful intermediates. Toluene removal efficiency increased with the TiO2 thickness (i.e., mass) until a maximum value of 500 nm, beyond which the removal efficiency decreased. This should be attributed to limitations on the rates of toluene decomposition imposed by radiation transport through the film and/or internal diffusion resistances, which can take place within the porous photocatalytic films.

Source

  • Journal Name: Applied Catalysis B - Environmental

Language

Item Type

Identifier

Unique identifying numbers for this article in the Digital Library or other systems.

  • Report No.: LBNL-2386E
  • Grant Number: DE-AC02-05CH11231
  • Office of Scientific & Technical Information Report Number: 971671
  • Archival Resource Key: ark:/67531/metadc931730

Collections

This article is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this article?

When

Dates and time periods associated with this article.

Creation Date

  • July 1, 2009

Added to The UNT Digital Library

  • Nov. 13, 2016, 7:26 p.m.

Description Last Updated

  • Jan. 4, 2017, 5:34 p.m.

Usage Statistics

When was this article last used?

Yesterday: 0
Past 30 days: 5
Total Uses: 26

Interact With This Article

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

International Image Interoperability Framework

IIF Logo

We support the IIIF Presentation API

Quici, Natalia; Vera, Maria L.; Choi, Hyeok; Puma, Gianluca Li; Dionysiou, Dionysios D.; Litter, Marta I. et al. Effect of Key Parameters on the Photocatalytic Oxidation of Toluene at Low Concentrations in Air under 254 + 185 nm UV Irradiation, article, July 1, 2009; Berkeley, California. (digital.library.unt.edu/ark:/67531/metadc931730/: accessed November 15, 2018), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.