(Cd,Mn)Te detectors for characterization of x-ray emissions generated during laser-driven fusion experiments

PDF Version Also Available for Download.

Description

We present our measurements of (Cd,Mn)Te photoconductive detectors (PCDs), fabricated for the goal of measuring both the temporal and spectral dependences of X-ray emissions generated from laser-illuminated targets during the inertial confinement fusion experiments. Our Cd{sub 1-x}Mn{sub x}Te (x = 0.05) single crystals, doped with V, were grown using a vertical Bridgman method and, subsequently, annealed in Cd for the highest resistivity ({approx}10{sup 10} {Omega}cm) and a good mobility-lifetime product ({approx}10{sup -3} cm{sup 2}/V). The 1-mm- and 2.3-mm-thick detectors were placed in the same housing as two 1-mm-thick diamond PCDs. All devices were pre-screened by a 7.6-mm-thick Be X-ray filter ... continued below

Creation Information

Cross, A. S.; Knauer, J. P.; Mycielski, A.; Kochanowska, D.; Wiktowska-Baran, M.; Jakiela, R. et al. October 19, 2008.

Context

This article is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. More information about this article can be viewed below.

Who

People and organizations associated with either the creation of this article or its content.

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this article. Follow the links below to find similar items on the Digital Library.

Description

We present our measurements of (Cd,Mn)Te photoconductive detectors (PCDs), fabricated for the goal of measuring both the temporal and spectral dependences of X-ray emissions generated from laser-illuminated targets during the inertial confinement fusion experiments. Our Cd{sub 1-x}Mn{sub x}Te (x = 0.05) single crystals, doped with V, were grown using a vertical Bridgman method and, subsequently, annealed in Cd for the highest resistivity ({approx}10{sup 10} {Omega}cm) and a good mobility-lifetime product ({approx}10{sup -3} cm{sup 2}/V). The 1-mm- and 2.3-mm-thick detectors were placed in the same housing as two 1-mm-thick diamond PCDs. All devices were pre-screened by a 7.6-mm-thick Be X-ray filter with a frequency cutoff of 1 keV. The incident shots from the OMEGA laser were 1-ns-long square pulses with energies ranging from 2.3 kJ to 22.6 kJ, and the PCDs were biased with 5000 V/cm. The response amplitudes and rise times of our (Cd,Mn)Te PCDs were comparable with the diamond detector performance, while the decay times were 4 to 10 times longer and in the 2-5 ns range. We observed two X-ray emission events separated by 1.24 ns. The first was identified as caused by heating of the target and creating a hot corona, while the second one was from the resulting compressed core. For comparison purposes, our testing was performed using {approx}1 keV X-ray photons, optimal for the diamond PCD. According to the presented simulations, however, at X-ray energies >10 keV diamond absorption efficiency drops to <50%, whereas for (Cd,Mn)Te the drop occurs at {approx}100 keV with near perfect, 100% absorption, up to 50 keV.

Source

  • IEEE Dresden 2008; Dresden, Germany; 20081019 through 20081025

Language

Item Type

Identifier

Unique identifying numbers for this article in the Digital Library or other systems.

  • Report No.: BNL--82064-2009-CP
  • Grant Number: DE-AC02-98CH10886
  • Office of Scientific & Technical Information Report Number: 950010
  • Archival Resource Key: ark:/67531/metadc929055

Collections

This article is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this article?

When

Dates and time periods associated with this article.

Creation Date

  • October 19, 2008

Added to The UNT Digital Library

  • Nov. 13, 2016, 7:26 p.m.

Description Last Updated

  • Sept. 25, 2017, 3:15 p.m.

Usage Statistics

When was this article last used?

Yesterday: 0
Past 30 days: 0
Total Uses: 1

Interact With This Article

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

Citations, Rights, Re-Use

Cross, A. S.; Knauer, J. P.; Mycielski, A.; Kochanowska, D.; Wiktowska-Baran, M.; Jakiela, R. et al. (Cd,Mn)Te detectors for characterization of x-ray emissions generated during laser-driven fusion experiments, article, October 19, 2008; United States. (digital.library.unt.edu/ark:/67531/metadc929055/: accessed November 24, 2017), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.