The diffusion of Kr/sup 85/ in two UO/sub 2/ powders was studied by performing a series of post-irradiation anneals on the powders. The emanation data were analyzed by considering the effect of sintering as well as the effect of a distribution of particle sizes within the sample. Measurements were made at 900 to 1500 deg C. The time at a temperature was between 8 and 24 hours. The diffusion coefficients for Kr/sup 85/ in the two powders are represented by the equations: D = 2.65 x 10/sup -4/ exp - 65,500/RT for UO/sub 2/ prepared from crushed UO/sub 2/ pellets …
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.
Description
The diffusion of Kr/sup 85/ in two UO/sub 2/ powders was studied by performing a series of post-irradiation anneals on the powders. The emanation data were analyzed by considering the effect of sintering as well as the effect of a distribution of particle sizes within the sample. Measurements were made at 900 to 1500 deg C. The time at a temperature was between 8 and 24 hours. The diffusion coefficients for Kr/sup 85/ in the two powders are represented by the equations: D = 2.65 x 10/sup -4/ exp - 65,500/RT for UO/sub 2/ prepared from crushed UO/sub 2/ pellets and, for a chemically prepared UO/sub 2/ powder, D = 4.9 x 10/sup -4/ exp - 73,800/RT. (auth)
This report is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.