The chemical decontamination of the ANL-2 Highpressure Water Loop at the MTR is described. A mixture of sodium hydroxide and potassium permanganate was first applied to oxidize partially and loosen the magnetite corrosion film on the loop surfaces. Next, the system was treated with a solution of Versenol 120 to remove and suspend the loosened oxide film. The third chemical treatment was a mixture of sulfamic acid, HEDTA, hydrazine, and Rodine 80. After the first two chemical treatments a brown residue remained, which was presumed to be manganese dioxide. The third solution completely removed all traces of residue from the …
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.
Description
The chemical decontamination of the ANL-2 Highpressure Water Loop at the MTR is described. A mixture of sodium hydroxide and potassium permanganate was first applied to oxidize partially and loosen the magnetite corrosion film on the loop surfaces. Next, the system was treated with a solution of Versenol 120 to remove and suspend the loosened oxide film. The third chemical treatment was a mixture of sulfamic acid, HEDTA, hydrazine, and Rodine 80. After the first two chemical treatments a brown residue remained, which was presumed to be manganese dioxide. The third solution completely removed all traces of residue from the first two treatments. After a delay of one MTR fuel cycle (three weeks) due to mechanical difficulties, the loop was operated for approximately 300 hours at 420 deg F and 380 psig with excess hydrogen to passivate the loop surfaces. Approximately 70% of the corrosion film was removed from the loop surfaces as a result of the chemical decontamination. (auth)
This report is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.