Ni ion damage in Cu and Nb Metadata

Metadata describes a digital item, providing (if known) such information as creator, publisher, contents, size, relationship to other resources, and more. Metadata may also contain "preservation" components that help us to maintain the integrity of digital files over time.


  • Main Title Ni ion damage in Cu and Nb


  • Author: Roberto, J.B.
    Creator Type: Personal
  • Author: Narayan, J.
    Creator Type: Personal


  • Name: Oak Ridge National Laboratory
    Place of Publication: Tennessee
    Additional Info: Oak Ridge National Lab., Tenn. (USA)


  • Creation: 1975-01-01


  • English


  • Content Description: Ni ion damage in Cu was studied using x-ray diffuse scattering and transmission electron microscopy, and in Nb using x-ray diffuse scattering. Single crystals of Cu and Nb were irradiated at room temperature to a fluence of 1.2 x 10$sup 13$/cm$sup 2$ at 60 MeV, and Cu was also irradiated to 5 x 10$sup 12$/cm$sup 2$ at 4 MeV. The x-ray diffuse scattering from loop-type defect clusters in the crystals was measured near several Bragg reflections in order to probe the depth distributions of the damage. In Cu, cluster size distributions derived from the x-ray measurements agreed well with TEM results. Comparison with fission reactor irradiations using the damage energy concept suggests similarities in retained damage between the neutron and Ni ion irradiations. (auth)
  • Physical Description: 8 p.


  • Keyword: Nickel Ions
  • Keyword: X- Ray Diffraction
  • Keyword: Electron Microscopy
  • Keyword: *Niobium-- Physical Radiation Effects
  • Keyword: Fast Neutrons
  • Keyword: N50240* --Metals, Ceramics, & Other Materials--Metals & Alloys--Radiation Effects
  • Keyword: Mev Range 01-10
  • Keyword: *Copper-- Physical Radiation Effects
  • STI Subject Categories: 360106* --Materials--Metals & Alloys--Radiation Effects
  • Keyword: Mev Range 10-100
  • Keyword: Ion Beams
  • Keyword: Comparative Evaluations
  • Keyword: Neutron Beams
  • Keyword: Monocrystals


  • Conference: International conference on radiation damage in metals, Gatlinburg, Tennessee, USA, 5 Oct 1975


  • Name: Office of Scientific & Technical Information Technical Reports
    Code: OSTI


  • Name: UNT Libraries Government Documents Department
    Code: UNTGD

Resource Type

  • Article


  • Text


  • Report No.: CONF-751006--13
  • Grant Number: None
  • Office of Scientific & Technical Information Report Number: 4144324
  • Archival Resource Key: ark:/67531/metadc866240


  • Display Note: Dep. NTIS