Elastic and plastic strains and the stress corrosion cracking of austenitic stainless steels. Progress report, April 30, 1975--December 30, 1975

PDF Version Also Available for Download.

Description

Homogeneous deformation of type 310 austenitic stainless steel only slightly influenced the corrosion potential in a boiling 3 percent NaCl aqueous environment. The difference in a deaerated solution was of the order of 25 mV and somewhat more for an aerated solution. Elastic strains appeared to have little or no influence on the corrosion potential for fully annealed as well as 10 percent and 25 percent homogeneously deformed 310 steel. Oxygen in the environment shifted the corrosion potential several hundred millivolts in the less active direction. The critical cracking potential in a deaerated 3 percent NaCl solution was approximately the ... continued below

Physical Description

20 p.

Creation Information

Troiano, A.R. December 1, 1975.

Context

This report is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. More information about this report can be viewed below.

Who

People and organizations associated with either the creation of this report or its content.

Author

Publisher

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this report. Follow the links below to find similar items on the Digital Library.

Description

Homogeneous deformation of type 310 austenitic stainless steel only slightly influenced the corrosion potential in a boiling 3 percent NaCl aqueous environment. The difference in a deaerated solution was of the order of 25 mV and somewhat more for an aerated solution. Elastic strains appeared to have little or no influence on the corrosion potential for fully annealed as well as 10 percent and 25 percent homogeneously deformed 310 steel. Oxygen in the environment shifted the corrosion potential several hundred millivolts in the less active direction. The critical cracking potential in a deaerated 3 percent NaCl solution was approximately the same for the annealed and homogeneously deformed specimens at approximately -125 mV SCE.

Physical Description

20 p.

Notes

Dep. NTIS

Source

  • Other Information: Orig. Receipt Date: 30-JUN-76

Language

Item Type

Identifier

Unique identifying numbers for this report in the Digital Library or other systems.

  • Report No.: COO--2576-2
  • Grant Number: E(11-1)-2576
  • DOI: 10.2172/4087844 | External Link
  • Office of Scientific & Technical Information Report Number: 4087844
  • Archival Resource Key: ark:/67531/metadc865251

Collections

This report is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this report?

When

Dates and time periods associated with this report.

Creation Date

  • December 1, 1975

Added to The UNT Digital Library

  • Sept. 16, 2016, 12:32 a.m.

Description Last Updated

  • Oct. 12, 2017, 2:58 p.m.

Usage Statistics

When was this report last used?

Yesterday: 0
Past 30 days: 1
Total Uses: 3

Interact With This Report

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

Citations, Rights, Re-Use

Troiano, A.R. Elastic and plastic strains and the stress corrosion cracking of austenitic stainless steels. Progress report, April 30, 1975--December 30, 1975, report, December 1, 1975; United States. (digital.library.unt.edu/ark:/67531/metadc865251/: accessed October 20, 2017), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.