BS>The aqueous corrosion of Mg alloys was investigated at 53 to 150 deg C. Corrosion rates rose rapidly with temperature, reaching about 3 mils per day at 150 deg C for AZ-31 STAMg-2.5 to 3.5 wt.% Al-0.7 to 1.3 wt.% Zn-0.2 wt.% Mn!. Additions of small amounts of Cu and/or Ni to the basic AZ-31 composition reduced the corrosion rate at 150 deg by a factor of about two. Sn may be advantageously substituted for Zn in AZ-31. Control of the pH in the range between 6 and 7 and maintenance of a fluoride concentration in the range between 1 …
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.
Description
BS>The aqueous corrosion of Mg alloys was investigated at 53 to 150 deg C. Corrosion rates rose rapidly with temperature, reaching about 3 mils per day at 150 deg C for AZ-31 STAMg-2.5 to 3.5 wt.% Al-0.7 to 1.3 wt.% Zn-0.2 wt.% Mn!. Additions of small amounts of Cu and/or Ni to the basic AZ-31 composition reduced the corrosion rate at 150 deg by a factor of about two. Sn may be advantageously substituted for Zn in AZ-31. Control of the pH in the range between 6 and 7 and maintenance of a fluoride concentration in the range between 1 and 10 ppm reduced the corrosion rate of AZ-31 to about 0.1 mil per day at 150 deg C. (auth)
This report is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.