Durability of Actinide Ceramic Waste Forms Under Conditions of Granitoid Rocks

PDF Version Also Available for Download.

Description

Three samples of {sup 239}Pu-{sup 241}Am-doped ceramics obtained from previous research were used for alteration experiments simulating corrosion of waste forms in ion-saturated solutions. These were ceramics based on: pyrochlore, (Ca,Hf,Pu,U,Gd){sub 2}Ti{sub 2}O{sub 7}, containing 10 wt.% Pu and 0.1 wt.% Am; zircon, (Zr,Pu)SiO{sub 4}, containing 5-6 wt.% Pu and 0.05 wt.% Am; cubic zirconia, (Zr,Gd,Pu)O{sub 2}, containing 10 wt.% Pu and 0.1 wt.% Am. All these samples were milled in an agate mortar to obtain powder with particle sizes less than 30 micron. Sample of granite taken from the depth 500-503 m was studied and then used for preparing ... continued below

Physical Description

5 pages

Creation Information

Burakov, B. E. & Anderson, E. B. February 26, 2002.

Context

This article is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. More information about this article can be viewed below.

Who

People and organizations associated with either the creation of this article or its content.

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this article. Follow the links below to find similar items on the Digital Library.

Description

Three samples of {sup 239}Pu-{sup 241}Am-doped ceramics obtained from previous research were used for alteration experiments simulating corrosion of waste forms in ion-saturated solutions. These were ceramics based on: pyrochlore, (Ca,Hf,Pu,U,Gd){sub 2}Ti{sub 2}O{sub 7}, containing 10 wt.% Pu and 0.1 wt.% Am; zircon, (Zr,Pu)SiO{sub 4}, containing 5-6 wt.% Pu and 0.05 wt.% Am; cubic zirconia, (Zr,Gd,Pu)O{sub 2}, containing 10 wt.% Pu and 0.1 wt.% Am. All these samples were milled in an agate mortar to obtain powder with particle sizes less than 30 micron. Sample of granite taken from the depth 500-503 m was studied and then used for preparing ion-saturated water solutions. A rock sample was ground, washed and classified. A fraction with particle size 0.10-0.25 mm was selected for alteration experiments. Powdered ceramic samples were separately placed into deionized water together with ground granite (approximately 1gram granite per 12-ml water) in special Teflon{trademark} vessels and set at 90 C in the oven for 3 months. After alteration experiments, the ceramic powders were studied by precise XRD analysis. Aqueous solutions and granite grains were analyzed for Am and Pu contents. The results show that alteration did not cause significant phase transformation in all ceramic samples. For all altered samples, the Am contents in aqueous solutions after experiments were similar (approximately n x 10{sup 2} Bq/ml) as well as Am amounts absorbed on granite grains (approximately n x 10{sup 5} Bq/g). Results on Pu contents were varied: for the solutions--from 60 Bq/ml for pyrochlore ceramic to 2.1 x 10{sup 3} Bq/ml for zircon ceramic; and for the absorption on granite--from 2.6 x 10{sup 4} Bq/g for zirconia ceramic to 1.4-6.8 x 10{sup 5} Bq/g for pyrochlore and zircon ceramics.

Physical Description

5 pages

Source

  • Waste Management 2002 Symposium, Tucson, AZ (US), 02/24/2002--02/28/2002

Language

Item Type

Identifier

Unique identifying numbers for this article in the Digital Library or other systems.

  • Report No.: none
  • Office of Scientific & Technical Information Report Number: 828347
  • Archival Resource Key: ark:/67531/metadc789073

Collections

This article is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this article?

When

Dates and time periods associated with this article.

Creation Date

  • February 26, 2002

Added to The UNT Digital Library

  • Dec. 3, 2015, 9:30 a.m.

Description Last Updated

  • April 27, 2016, 1:24 p.m.

Usage Statistics

When was this article last used?

Yesterday: 0
Past 30 days: 0
Total Uses: 3

Interact With This Article

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

International Image Interoperability Framework

IIF Logo

We support the IIIF Presentation API

Burakov, B. E. & Anderson, E. B. Durability of Actinide Ceramic Waste Forms Under Conditions of Granitoid Rocks, article, February 26, 2002; Tucson, Arizona. (digital.library.unt.edu/ark:/67531/metadc789073/: accessed August 15, 2018), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.