Aspects of the SrO-CuO-TiO2 Ternary System Related to the Deposition of SrTiO3 and Copper-Doped SrTiO3 Thin-Film Buffer Layers

PDF Version Also Available for Download.

Description

YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) coated conductors are promising materials for large-scale superconductivity applications. One version of a YBCO coated conductor is based on ion beam assisted deposition (IBAD) of magnesium oxide (MgO) onto polycrystalline metal substrates. SrTiO{sub 3} (STO) is often deposited by physical vapor deposition (PVD) methods as a buffer layer between the YBCO and IBAD MgO due to its chemical stability and lattice mismatch of only {approx}1.5% with YBCO. In this work, some aspects of the stability of STO with respect to copper (Cu) and chemical solution deposition of STO on IBAD MgO templates were examined. Solubility ... continued below

Physical Description

145 pages

Creation Information

Ayala, A. December 20, 2004.

Context

This thesis or dissertation is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. It has been viewed 16 times . More information about this document can be viewed below.

Who

People and organizations associated with either the creation of this thesis or dissertation or its content.

Author

Sponsor

Publisher

  • Los Alamos National Laboratory
    Publisher Info: Los Alamos National Lab., Los Alamos, NM (United States)
    Place of Publication: Los Alamos, New Mexico

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this thesis or dissertation. Follow the links below to find similar items on the Digital Library.

Description

YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) coated conductors are promising materials for large-scale superconductivity applications. One version of a YBCO coated conductor is based on ion beam assisted deposition (IBAD) of magnesium oxide (MgO) onto polycrystalline metal substrates. SrTiO{sub 3} (STO) is often deposited by physical vapor deposition (PVD) methods as a buffer layer between the YBCO and IBAD MgO due to its chemical stability and lattice mismatch of only {approx}1.5% with YBCO. In this work, some aspects of the stability of STO with respect to copper (Cu) and chemical solution deposition of STO on IBAD MgO templates were examined. Solubility limits of Cu in STO were established by processing Cu-doped STO powders by conventional bulk preparation techniques. The maximum solubility of Cu in STO was {approx}1% as determined by transmission electron microscopy (TEM) and Rietveld refinements of x-ray diffraction (XRD) data. XRD analysis, performed in collaboration with NIST, on powder compositions on the STO/SrCuO{sub 2} tie line did not identify any ternary phases. SrCu{sub 0.10}Ti{sub 0.90}O{sub y} buffer layers were prepared by pulsed laser deposition (PLD) and CSD on IBAD MgO flexible metallic textured tapes. TEM analysis of a {approx}100 nm thick SrCu{sub 0.10}Ti{sub 0.90}O{sub y} buffer layer deposited by PLD showed a smooth Cu-doped STO/MgO interface. A {approx}600 nm thick YBCO film, deposited onto the SrCu{sub 0.10}Ti{sub 0.90}O{sub y} buffer by PLD, exhibited a T{sub c} of 87 K and critical current density (J{sub c}) of {approx}1 MA/cm{sup 2}. STO and Cu-doped STO thin films by CSD were {approx}30 nm thick. The in plane alignment (FWHM) after deposition of the STO improved by {approx}1{sup o} while it degraded by {approx}2{sup o} with the SrCu{sub 0.05}TiO{sub y} buffer. YBCO was deposited by PLD on the STO and SrCu{sub 0.05}TiO{sub y} buffers. The in plane alignment (FWHM) of the YBCO with the STO buffer layer slightly improved while that of the YBCO with the SrCu{sub 0.05}TiO{sub y} buffer layer remained constant. A goal of the CSD approach to fabrication of coated conductors is process simplicity. In this study, single layer textured films were obtained without a nucleating seed layer that has been deemed necessary by several investigators. These results indicate that Cu-doped STO buffer layers deposited by PLD or CSD are compatible with IBAD MgO and YBCO and that CSD is a viable approach to coated conductor fabrication.

Physical Description

145 pages

Notes

OSTI as DE00836697

Source

  • Other Information: TH: Thesis (Ph.D.); Submitted to the Univ. of New Mexico, Albuquerque, NM (US)

Language

Identifier

Unique identifying numbers for this document in the Digital Library or other systems.

  • Report No.: LA-14197-T
  • Grant Number: W-7405-ENG-36
  • Office of Scientific & Technical Information Report Number: 836697
  • Archival Resource Key: ark:/67531/metadc785231

Collections

This document is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this thesis or dissertation?

When

Dates and time periods associated with this thesis or dissertation.

Creation Date

  • December 20, 2004

Added to The UNT Digital Library

  • Dec. 3, 2015, 9:30 a.m.

Description Last Updated

  • March 24, 2016, 5:18 p.m.

Usage Statistics

When was this document last used?

Yesterday: 0
Past 30 days: 3
Total Uses: 16

Interact With This Thesis Or Dissertation

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

Citations, Rights, Re-Use

Ayala, A. Aspects of the SrO-CuO-TiO2 Ternary System Related to the Deposition of SrTiO3 and Copper-Doped SrTiO3 Thin-Film Buffer Layers, thesis or dissertation, December 20, 2004; Los Alamos, New Mexico. (digital.library.unt.edu/ark:/67531/metadc785231/: accessed October 22, 2017), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.