SCC INITIATION AND GROWTH RATE STUDIES ON TITANIUM GRADE 7 AND BASE METAL, WELDED, AND AGED ALLOY 22 IN CONCENTRATED GROUNDWATER

PDF Version Also Available for Download.

Description

The stress corrosion crack initiation and growth rate response was evaluated on as-received, as-welded, cold worked and aged Alloy 22 (UNS N06022) and titanium Grades 7 (UNS R52400), 28 (UNS R55323) and 29 (UNS R56404) at 105-165 C in various aerated, concentrated groundwater environments. Time-to-failure experiments on actively-loaded tensile specimens at 105 C evaluated the effects of applied stress, welding, surface finish, shot peening, cold work, crevicing, and aging treatments in Alloy 22 (UNS N06022), and found these materials to be highly resistant to SCC (none observed). Long-term U-bend data at 165 C corroborated these findings. Titanium Grade 7 and ... continued below

Creation Information

Payer, J.H. August 1, 2005.

Context

This report is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. It has been viewed 15 times . More information about this report can be viewed below.

Who

People and organizations associated with either the creation of this report or its content.

Author

Publisher

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this report. Follow the links below to find similar items on the Digital Library.

Description

The stress corrosion crack initiation and growth rate response was evaluated on as-received, as-welded, cold worked and aged Alloy 22 (UNS N06022) and titanium Grades 7 (UNS R52400), 28 (UNS R55323) and 29 (UNS R56404) at 105-165 C in various aerated, concentrated groundwater environments. Time-to-failure experiments on actively-loaded tensile specimens at 105 C evaluated the effects of applied stress, welding, surface finish, shot peening, cold work, crevicing, and aging treatments in Alloy 22 (UNS N06022), and found these materials to be highly resistant to SCC (none observed). Long-term U-bend data at 165 C corroborated these findings. Titanium Grade 7 and stainless steels were also included in the 105 C test matrix. Long term crack growth rate data showed stable crack growth in titanium Grade 7. Recent creep tests in air confirm literature data that these alloys are quite susceptible to creep failure, even below the yield stress, and it is unclear whether cracking in SCC tests is only accelerated by the creep response, or whether creep is responsible for cracking. Alloy 22 exhibited stable growth rates under ''gentle'' cyclic loading, but was prone to crack arrest at fully static loading. No effect of Pb additions was observed.

Language

Item Type

Identifier

Unique identifying numbers for this report in the Digital Library or other systems.

  • Report No.: NA
  • Grant Number: NA
  • DOI: 10.2172/859399 | External Link
  • Office of Scientific & Technical Information Report Number: 859399
  • Archival Resource Key: ark:/67531/metadc779941

Collections

This report is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this report?

When

Dates and time periods associated with this report.

Creation Date

  • August 1, 2005

Added to The UNT Digital Library

  • Dec. 3, 2015, 9:30 a.m.

Description Last Updated

  • Dec. 8, 2016, 9:46 p.m.

Usage Statistics

When was this report last used?

Yesterday: 0
Past 30 days: 0
Total Uses: 15

Interact With This Report

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

Citations, Rights, Re-Use

Payer, J.H. SCC INITIATION AND GROWTH RATE STUDIES ON TITANIUM GRADE 7 AND BASE METAL, WELDED, AND AGED ALLOY 22 IN CONCENTRATED GROUNDWATER, report, August 1, 2005; Oak Ridge, Tennessee. (digital.library.unt.edu/ark:/67531/metadc779941/: accessed May 21, 2018), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.