IMPERMEABLE THIN AL2O3 OVERLAY FOR TBC PROTECTION FROM SULFATE AND VANADATE ATTACK IN GAS TURBINES

PDF Version Also Available for Download.

Description

In order to improve the hot corrosion resistance of conventional YSZ TBC system, a dense and continues overlay of Al{sub 2}O{sub 3} coating of about 25 {micro}m thick was deposited on the surface of TBC by EB-PVD and high velocity oxy-fuel (HVOF) spray techniques. Hot corrosion tests were carried out on the TBC with and without Al{sub 2}O{sub 3} coating in molten salts mixtures (Na{sub 2}SO{sub 4} + 5% V{sub 2}O5) at 950 C for 10h. The microstructures of TBC and overlay before and after exposure were examined by means of scanning electron microscopy (SEM), energy-dispersive X-ray spectrometer (EDX), X-ray ... continued below

Physical Description

14 pages

Creation Information

Mao, Scott X. August 31, 2002.

Context

This report is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. More information about this report can be viewed below.

Who

People and organizations associated with either the creation of this report or its content.

Author

Sponsor

Publishers

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this report. Follow the links below to find similar items on the Digital Library.

Description

In order to improve the hot corrosion resistance of conventional YSZ TBC system, a dense and continues overlay of Al{sub 2}O{sub 3} coating of about 25 {micro}m thick was deposited on the surface of TBC by EB-PVD and high velocity oxy-fuel (HVOF) spray techniques. Hot corrosion tests were carried out on the TBC with and without Al{sub 2}O{sub 3} coating in molten salts mixtures (Na{sub 2}SO{sub 4} + 5% V{sub 2}O5) at 950 C for 10h. The microstructures of TBC and overlay before and after exposure were examined by means of scanning electron microscopy (SEM), energy-dispersive X-ray spectrometer (EDX), X-ray diffraction (XRD) and secondary ion mass spectrometry (SIMS). It has been found that TBC will react with V{sub 2}O{sub 5} to form YVO{sub 4}. A substantial amount of M-phase of ZrO{sub 2} was formed due to the leaching of Y{sub 2}O{sub 3} from YSZ. During hot corrosion test, there were no significant interactions between overlay Al{sub 2}O{sub 3} coating and molten salts. After exposure, the alumina coating, especially produced by HVOF, was still very dense and cover the surface of YSZ, although they had been translated to {alpha}-Al{sub 2}O{sub 3} from original {gamma}-Al{sub 2}O{sub 3}. As a result, Al{sub 2}O{sub 3} overlay coating decreased the penetration of salts into the YSZ and prevented the YSZ from the attack by molten salts containing vanadium. Accordingly, only a few M-phase was formed in YSZ TBC, compared with TBC without overlay coating. The penetration of salts into alumina coating was thought to be through microcracks formed in overlay Al{sub 2}O{sub 3} coating and at the interface between alumina and zirconia due to the presence of tensile stress in the alumina coating. In the next year, we will study the mechanisms of cracking of the overlay Al{sub 2}O{sub 3} layer. The hot corrosion test of TBC with EB-PVD deposited Al{sub 2}O{sub 3} coating will be again performed. However before hot corrosion tests, the post-annealing will be carried out in vacuum (residual pressure 10{sup -3} Pa) at 1273K for 1h in order to transform the as-sputtered Al{sub 2}O{sub 3} overlay to crystalline {alpha}-Al{sub 2}O{sub 3} overlay. The effect of thickness of Al{sub 2}O{sub 3} coating on hot corrosion resistance will also be investigated. We will prepare Al{sub 2}O{sub 3} coating by sol-gel method. The corrosion resistance of TBC with sol-gel Al{sub 2}O{sub 3} coating will be determined and discussed with the results of TBC with EB-PVD and HVOF Al{sub 2}O{sub 3} coating.

Physical Description

14 pages

Notes

OSTI as DE00802865

Source

  • Other Information: PBD: 31 Aug 2002

Language

Item Type

Identifier

Unique identifying numbers for this report in the Digital Library or other systems.

  • Report No.: FC26-01NT41189--04
  • Grant Number: FC26-01NT41189
  • DOI: 10.2172/802865 | External Link
  • Office of Scientific & Technical Information Report Number: 802865
  • Archival Resource Key: ark:/67531/metadc742536

Collections

This report is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

What responsibilities do I have when using this report?

When

Dates and time periods associated with this report.

Creation Date

  • August 31, 2002

Added to The UNT Digital Library

  • Oct. 19, 2015, 7:39 p.m.

Description Last Updated

  • March 30, 2016, 12:50 p.m.

Usage Statistics

When was this report last used?

Yesterday: 0
Past 30 days: 0
Total Uses: 4

Interact With This Report

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

Citations, Rights, Re-Use

Mao, Scott X. IMPERMEABLE THIN AL2O3 OVERLAY FOR TBC PROTECTION FROM SULFATE AND VANADATE ATTACK IN GAS TURBINES, report, August 31, 2002; Pittsburgh, Pennsylvania. (digital.library.unt.edu/ark:/67531/metadc742536/: accessed August 19, 2017), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.