Fe-Al Weld Overlay and High Velocity Oxy-Fuel Thermal Spray Coatings for Corrosion Protection of Waterwalls in Fossil Fired Plants with Low NOx Burners

PDF Version Also Available for Download.

Description

Iron-aluminum-chromium coatings were investigated to determine the best candidates for coatings of boiler tubes in Low NOx fossil fueled power plants. Ten iron-aluminum-chromium weld claddings with aluminum concentrations up to 10wt% were tested in a variety of environments to evaluate their high temperature corrosion resistance. The weld overlay claddings also contained titanium additions to investigate any beneficial effects from these ternary and quaternary alloying additions. Several High-Velocity Oxy-Fuel (HVOF) thermal spray coatings with higher aluminum concentrations were investigated as well. Gaseous corrosion testing revealed that at least 10wt%Al is required for protection in the range of environments examined. Chromium additions ... continued below

Physical Description

122 pages

Creation Information

Regina, J.R. February 8, 2002.

Context

This report is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. It has been viewed 26 times , with 9 in the last month . More information about this report can be viewed below.

Who

People and organizations associated with either the creation of this report or its content.

Author

Sponsor

Publisher

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this report. Follow the links below to find similar items on the Digital Library.

Description

Iron-aluminum-chromium coatings were investigated to determine the best candidates for coatings of boiler tubes in Low NOx fossil fueled power plants. Ten iron-aluminum-chromium weld claddings with aluminum concentrations up to 10wt% were tested in a variety of environments to evaluate their high temperature corrosion resistance. The weld overlay claddings also contained titanium additions to investigate any beneficial effects from these ternary and quaternary alloying additions. Several High-Velocity Oxy-Fuel (HVOF) thermal spray coatings with higher aluminum concentrations were investigated as well. Gaseous corrosion testing revealed that at least 10wt%Al is required for protection in the range of environments examined. Chromium additions were beneficial in all of the environments, but additions of titanium were beneficial only in sulfur rich atmospheres. Similar results were observed when weld claddings were in contact with corrosive slag while simultaneously, exposed to the corrosive environments. An aluminum concentration of 10wt% was required to prevent large amounts of corrosion to take place. Again chromium additions were beneficial with the greatest corrosion protection occurring for welds containing both 10wt%Al and 5wt%Cr. The exposed thermal spray coatings showed either significant cracking within the coating, considerable thickness loss, or corrosion products at the coating substrate interface. Therefore, the thermal spray coatings provided the substrate very little protection. Overall, it was concluded that of the coatings studied weld overlay coatings provide superior protection in these Low NOx environments; specifically, the ternary weld composition of 10wt%Al and 5wt%Cr provided the best corrosion protection in all of the environments tested.

Physical Description

122 pages

Source

  • Other Information: PBD: 8 Feb 2002

Language

Item Type

Identifier

Unique identifying numbers for this report in the Digital Library or other systems.

  • Report No.: ORNL/SUB/95-SU604/04
  • Grant Number: AC05-00OR22725
  • DOI: 10.2172/814323 | External Link
  • Office of Scientific & Technical Information Report Number: 814323
  • Archival Resource Key: ark:/67531/metadc737861

Collections

This report is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this report?

When

Dates and time periods associated with this report.

Creation Date

  • February 8, 2002

Added to The UNT Digital Library

  • Oct. 18, 2015, 6:40 p.m.

Description Last Updated

  • March 30, 2016, 8:23 p.m.

Usage Statistics

When was this report last used?

Yesterday: 1
Past 30 days: 9
Total Uses: 26

Interact With This Report

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

Citations, Rights, Re-Use

Regina, J.R. Fe-Al Weld Overlay and High Velocity Oxy-Fuel Thermal Spray Coatings for Corrosion Protection of Waterwalls in Fossil Fired Plants with Low NOx Burners, report, February 8, 2002; United States. (digital.library.unt.edu/ark:/67531/metadc737861/: accessed December 11, 2017), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.