Can Laterally Overgrown GaN Layers be free of Structural Defects?
D. Cherns and Z. Liliental-Weber*
H.H. Wills Physics Laboratory, University of Bristol, Tyndall Avenue, Bristol BS8 1TL, UK
*permanent address: Lawrence Berkeley Laboratory, Materials Science Division, Berkeley, CA
94720, USA
Abstract
Transmission electron microscopy has been used to examine dislocations present in an
epitaxial laterally overgrown (ELOG) sample of GaN grown on (0001)sapphire. Studies of both
plan-view and cross-sectional samples revealed arrays of dislocations present in the (11-20)
boundary between the seed and the wing (overgrown) material and at the meeting front between
adjacent wings, as well as dislocations in the form of half-loops extending into the wing regions.
Both the boundary and half-loop dislocations had 1/3<11-20> Burgers vectors which were either
perpendicular (boundary dislocations) or at 300 (half-loops) to the boundary plane. Large angle
convergent beam electron diffraction was used to show that the boundary dislocations and half-
loops correlated respectively with tilts and twists of the wing material about (11-20). A model is
proposed whereby the half-loops are generated from threading dislocations by shear stresses
acting along the stripe direction. The origin, and elimination, of these stresses is discussed.
Introduction
The epitaxial lateral overgrowth (ELOG) method was introduced in order to reduce the
density of threading dislocations generated in (0001)GaN films grown on highly lattice-
mismatched substrates such as (0001)sapphire. In the ELOG method, a mask, such as SiO2, is
deposited on a part-grown GaN layer. On resuming the growth, GaN does not nucleate on the
mask material. Growth then proceeds laterally from seed columns of GaN which grow through
gaps etched into the mask. Eventually, the GaN "wings" meet to produce a continuous film.
Provided threading dislocations continue to propagate in the seed material close to the c-axis as
in conventional GaN growth, the wing regions should be substantially dislocation-free.
It is now clear that this simple model of ELOG growth does hold entirely, with
significant, if lower, densities of dislocations reported for the wing material. Estimates vary
widely, from, for example, below 106 cm 2 [1] to nearly 108 cm 2 [2], with dislocation densities in
the seed material in the range 109 - 1010 cm 2. In addition, some observations show significant
bending of the wings, which may lead to the generation of new defects [3]. Such behaviour may
result from the high stresses generated by thermal mismatch between the GaN and the mask
material [4].
In this paper, we use transmission electron microscopy (TEM) and large angle
convergent beam electron diffraction (LACBED) to correlate the presence of dislocations in the
wing regions of an ELOG sample with measurements of the local strain. A new mechanism of
dislocation propagation in the wing material is proposed which is driven by shear stresses and
involves both glide and climb. The implications of the results for reducing dislocation densities
are considered.
Upcoming Pages
Here’s what’s next.
Search Inside
This article can be searched. Note: Results may vary based on the legibility of text within the document.
Tools / Downloads
Get a copy of this page or view the extracted text.
Citing and Sharing
Basic information for referencing this web page. We also provide extended guidance on usage rights, references, copying or embedding.
Reference the current page of this Article.
Cherns, D. & Liliental-Weber, Z. Can laterally overgrown GaN layers be free of structural defects?, article, July 31, 2002; Berkeley, California. (https://digital.library.unt.edu/ark:/67531/metadc735952/m1/1/: accessed April 25, 2024), University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu; crediting UNT Libraries Government Documents Department.