Thin-film photovoltaic partnership -- CIS-based thin film PV technology: Final technical report, September 1995--December 1998

PDF Version Also Available for Download.

Description

Siemens Solar Industries (SSI) achieved outstanding progress toward NREL/DOE goals during this subcontract. The statistical process control methodology was applied, and it demonstrated process reproducibility and yields for a 10-cm {times} 10-cm substrate size baseline process. Based on an understanding of the importance of materials of construction and the physical layout for absorber formation reactors, SSI designed and built a replacement large-area reactor based on a more direct scale-up of the baseline reactor. While designing and building the new large-area reactor, SSI defined and demonstrated new package designs to combine 10-cm {times} 30-cm circuit plates into one package; this allowed ... continued below

Physical Description

vp.

Creation Information

Tarrant, D.E. & Gay, R.R. October 26, 1999.

Context

This report is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. More information about this report can be viewed below.

Who

People and organizations associated with either the creation of this report or its content.

Sponsor

Publisher

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this report. Follow the links below to find similar items on the Digital Library.

Description

Siemens Solar Industries (SSI) achieved outstanding progress toward NREL/DOE goals during this subcontract. The statistical process control methodology was applied, and it demonstrated process reproducibility and yields for a 10-cm {times} 10-cm substrate size baseline process. Based on an understanding of the importance of materials of construction and the physical layout for absorber formation reactors, SSI designed and built a replacement large-area reactor based on a more direct scale-up of the baseline reactor. While designing and building the new large-area reactor, SSI defined and demonstrated new package designs to combine 10-cm {times} 30-cm circuit plates into one package; this allowed SSI to deliver large-area prototype modules to NREL for evaluation, and to introduce the first CIS-based products--5-watt (ST5) and 10-watt (ST10) modules. After completion of the new large-area reactor, all processes were scaled to a 30-cm {times} 120-cm plate size. Subsequently, only large 30-cm {times} 120-cm circuit plates were fabricated for 30-cm {times} 120-cm prototype modules or, after cutting the large circuit plates into smaller circuit plates, for the two new CIS-based products. The scaled process exhibits generally good control for extended periods with periodic shifts in the short-term process average that appears to result from batch-to-batch variability in precursor or base electrode preparation. Similarly, periodic shunting along the laser-scribed pattern lines in the Mo base electrode appears to result from batch-to-batch variability in base electrode preparation. Significant progress was made in understanding transient effects in CIS devices. Transient effects are important for many topics, including accelerated testing, process definition, measurement protocols, process predictability, interpretation of experimental test results, and understanding of device structures. Long-term outdoor stability of CIS continues to be demonstrated at NREL where 30-cm {times} 30-cm and 30-cm {times} 120-cm modules have undergone testing for more than ten years. SSI delivered two sets of upgraded modules for 1-kW arrays to the NREL Outdoor Test Facility. Improvements in efficiency and the temperature coefficient for power were demonstrated for these modules with sulfur incorporated to form a graded (Cu(In,Ga)(Se,S){sub 2}) absorber. The NREL-measured average module efficiency at standard test conditions is 11.4% for the second array, and the efficiency of all modules far exceeds the DOE year 2000 goal of 10% for commercial CIS modules. SSI demonstrated a succession of NREL-confirmed world-record efficiencies culminating in demonstration of an 11.8 %-efficient, large-area, 3,651-cm{sup 2} module.

Physical Description

vp.

Source

  • Other Information: PBD: 26 Oct 1999

Language

Item Type

Identifier

Unique identifying numbers for this report in the Digital Library or other systems.

  • Report No.: NREL/SR-520-27148
  • Grant Number: AC36-99GO10337
  • DOI: 10.2172/752655 | External Link
  • Office of Scientific & Technical Information Report Number: 752655
  • Archival Resource Key: ark:/67531/metadc704687

Collections

This report is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this report?

When

Dates and time periods associated with this report.

Creation Date

  • October 26, 1999

Added to The UNT Digital Library

  • Sept. 12, 2015, 6:31 a.m.

Description Last Updated

  • March 31, 2016, 5:50 p.m.

Usage Statistics

When was this report last used?

Yesterday: 0
Past 30 days: 0
Total Uses: 3

Interact With This Report

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

International Image Interoperability Framework

IIF Logo

We support the IIIF Presentation API

Tarrant, D.E. & Gay, R.R. Thin-film photovoltaic partnership -- CIS-based thin film PV technology: Final technical report, September 1995--December 1998, report, October 26, 1999; Golden, Colorado. (digital.library.unt.edu/ark:/67531/metadc704687/: accessed November 19, 2018), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.