Laser conditioning study of KDP on the optical sciences laser using large area beams

PDF Version Also Available for Download.

Description

Considerable attention has been paid over the years to the problem of growing high purity KDP and KD*P to meet threshold requirements on succeeding generations of inertial confinement fusion lasers at LLNL. While damage thresholds for these materials have increased over time, the current National Ignition Facility (NIF) maximum fluence requirement (redline) for KD*P frequency triplers of 14.3 J/cm{sup 2} at 351 nm, 3 ns has not been reached without laser (pre)conditioning. It is reasonable to assume that, despite the rapid increase in damage thresholds for rapidly grown crystals, -a program of large scale conditioning of the 192 NIF triplers ... continued below

Physical Description

16 p.

Creation Information

Runkel, M.; DeYoreo, J.; Sell, W. & Milam, D. December 20, 1997.

Context

This article is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. More information about this article can be viewed below.

Who

People and organizations associated with either the creation of this article or its content.

Sponsor

Publisher

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this article. Follow the links below to find similar items on the Digital Library.

Description

Considerable attention has been paid over the years to the problem of growing high purity KDP and KD*P to meet threshold requirements on succeeding generations of inertial confinement fusion lasers at LLNL. While damage thresholds for these materials have increased over time, the current National Ignition Facility (NIF) maximum fluence requirement (redline) for KD*P frequency triplers of 14.3 J/cm{sup 2} at 351 nm, 3 ns has not been reached without laser (pre)conditioning. It is reasonable to assume that, despite the rapid increase in damage thresholds for rapidly grown crystals, -a program of large scale conditioning of the 192 NIF triplers will be required. Small area ramp (R/1) tests on single sites indicate that KDP damage thresholds can be raised on average up to 1.5X the unconditioned values. Unpublished LLNL 3{omega} raster conditioning studies on KDP, however, have not conclusively shown that off-line conditioning is feasible for KD*P. Consequently, investigating the feasibility of on-line conditioning of NIF triplers at 3{omega} has become a high priority for the KDP damage group at LLNL. To investigate the feasibility of on-line conditioning we performed a series of experiments using the Optical Sciences Laser (OSL) on numerous samples of conventional and rapid growth KDP and KD*P. The experiment entailed exposing sites on each sample to a range of ramped shot (N/l) sequences starting at average fluences of -2 J/cm{sup 2} (in a 7 mm ``top hat`` beam @ 351 nm, 3 ns) up to peak fluences of approximately 13 J/cm{sup 2}. Test results indicated that the most effective conditioning procedure entailed a 7-8 shot ramp starting at 2 J/cm{sup 2} and ending at 12-13 J/cm{sup 2}. The pinpoint onset fluence for the 8/1 tests was 1.4 times that of the unconditioned site. Damage evolution appears to be exponential as a function of increasing fluence. When damage occurs after conditioning however, pinpoint density evolution exhibits a greater slope than less conditioned sites. The overall reduction in the total pinpoint number can be as high as 30OX. Despite laser conditioning , the pinpoint onset for the samples considered is below the NIF redline fluence of 14.3 J/cm{sup 2}. In addition, the exponential pinpoint evolution curves indicate that damage levels at NIF redline fluences will be on the order of 10{sup 4} pinpoints/mm{sup 2}. This suggests that there will be significant damage in NIP triplers, however, substantial damage has not been observed in the large Beamlet tripler (conventionally grown KD*P) under similar exposure conditions. By applying the OSL damage evolution curves to model NIF THG output spatial profiles it is possible to show damage in NIF triplers will be slight, consisting of isolated clusters with a few pinpoints at high fluence portions of the beam. This prediction has been verified by scatter mapping the 37 cm Beamlet tripler crystal. These results will be discussed in a future memo. These results indicate the feasibility of on-line conditioning for the NIF laser.

Physical Description

16 p.

Notes

INIS; OSTI as DE98052076

Other: FDE: PDF; PL:

Source

  • 29. annual Boulder damage symposium on optical materials for high power lasers, Boulder, CO (United States), 6-8 Oct 1997

Language

Item Type

Identifier

Unique identifying numbers for this article in the Digital Library or other systems.

  • Other: DE98052076
  • Report No.: UCRL-JC--128352
  • Report No.: CONF-9710116--
  • Grant Number: W-7405-ENG-48
  • Office of Scientific & Technical Information Report Number: 305309
  • Archival Resource Key: ark:/67531/metadc676085

Collections

This article is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this article?

When

Dates and time periods associated with this article.

Creation Date

  • December 20, 1997

Added to The UNT Digital Library

  • July 25, 2015, 2:20 a.m.

Description Last Updated

  • April 10, 2017, 2:01 p.m.

Usage Statistics

When was this article last used?

Yesterday: 0
Past 30 days: 0
Total Uses: 8

Interact With This Article

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

International Image Interoperability Framework

IIF Logo

We support the IIIF Presentation API

Runkel, M.; DeYoreo, J.; Sell, W. & Milam, D. Laser conditioning study of KDP on the optical sciences laser using large area beams, article, December 20, 1997; California. (digital.library.unt.edu/ark:/67531/metadc676085/: accessed September 26, 2018), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.