Long-term corrosion/oxidation studies under controlled humidity conditions

PDF Version Also Available for Download.

Description

Independent of thermal loading scenarios, the waste packages at the potential repository at Yucca Mountain, Nevada will be exposed to environmental conditions where there is the possibility of significant water film formation occurring on the waste packages. Water films can cause aggressive aqueous film electrochemical corrosion on susceptible metals or alloys. Water film formation will be facilitated when relative humidities are high, when hygroscopic salts are present on the surfaces, when corrosion products are hygroscopic, and when particles form crevices with the surfaces (capillary effect). Also certain gaseous contaminants, such as, NO{sub x} and SO{sub 2}, can facilitate water film ... continued below

Physical Description

1352 Kilobytes pages

Creation Information

Gdowski, G. October 13, 1997.

Context

This report is part of the collection entitled: Office of Scientific & Technical Information Technical Reports and was provided by UNT Libraries Government Documents Department to Digital Library, a digital repository hosted by the UNT Libraries. More information about this report can be viewed below.

Who

People and organizations associated with either the creation of this report or its content.

Author

Sponsor

Publisher

Provided By

UNT Libraries Government Documents Department

Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.

Contact Us

What

Descriptive information to help identify this report. Follow the links below to find similar items on the Digital Library.

Description

Independent of thermal loading scenarios, the waste packages at the potential repository at Yucca Mountain, Nevada will be exposed to environmental conditions where there is the possibility of significant water film formation occurring on the waste packages. Water films can cause aggressive aqueous film electrochemical corrosion on susceptible metals or alloys. Water film formation will be facilitated when relative humidities are high, when hygroscopic salts are present on the surfaces, when corrosion products are hygroscopic, and when particles form crevices with the surfaces (capillary effect). Also certain gaseous contaminants, such as, NO{sub x} and SO{sub 2}, can facilitate water film formation. It should be noted that water film formation can occur at isolated spots (e.g. surface defects and salt particles) and need not cover the entire surface for electrochemical corrosion to occur. This activity will characterize the long term corrosion of metal specimens at two nominal relative humidities (50 and 85%) and at 80 C. Under the low relative humidity (50%) condition, water film formation is expected to be limited and therefore aqueous film electrochemical corrosion is expected also to be limited. Under the high relative humidity (85%) condition, significant water film formation is expected to occur under some test conditions, and subsequently aqueous film electrochemical corrosion will occur on susceptible materials.

Physical Description

1352 Kilobytes pages

Source

  • Other Information: PBD: 13 Oct 1997

Language

Item Type

Identifier

Unique identifying numbers for this report in the Digital Library or other systems.

  • Report No.: UCRL-ID-132291
  • Grant Number: W-7405-ENG-48
  • DOI: 10.2172/2801 | External Link
  • Office of Scientific & Technical Information Report Number: 2801
  • Archival Resource Key: ark:/67531/metadc669873

Collections

This report is part of the following collection of related materials.

Office of Scientific & Technical Information Technical Reports

Reports, articles and other documents harvested from the Office of Scientific and Technical Information.

Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.

What responsibilities do I have when using this report?

When

Dates and time periods associated with this report.

Creation Date

  • October 13, 1997

Added to The UNT Digital Library

  • June 29, 2015, 9:42 p.m.

Description Last Updated

  • Sept. 25, 2017, 4:34 p.m.

Usage Statistics

When was this report last used?

Yesterday: 0
Past 30 days: 0
Total Uses: 4

Interact With This Report

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

Citations, Rights, Re-Use

Gdowski, G. Long-term corrosion/oxidation studies under controlled humidity conditions, report, October 13, 1997; California. (digital.library.unt.edu/ark:/67531/metadc669873/: accessed October 17, 2017), University of North Texas Libraries, Digital Library, digital.library.unt.edu; crediting UNT Libraries Government Documents Department.