A Novel Process for GeSi Thin Film Synthesis

PDF Version Also Available for Download.

Description

A unique process of fabricating a strained layer GexSi1-x on insulator is demonstrated. Such strained heterostructures are useful in the fabrication of high-mobility transistors. This technique incorporates well-established silicon processing technology e.g., ion implantation and thermal oxidation. A dilute GeSi layer is initially formed by implanting Ge+ into a silicon-on-insulator (SOI) substrate. Thermal oxidation segregates the Ge at the growing oxide interface to form a distinct GexSi1-x thin-film with a composition that can be tailored by controlling the oxidation parameters (e.g. temperature and oxidation ambient). In addition, the film thickness can be controlled by implantation fluence, which is important since ... continued below

Creation Information

Hossain, Khalid December 2007.

Context

This dissertation is part of the collection entitled: UNT Theses and Dissertations and was provided by UNT Libraries to Digital Library, a digital repository hosted by the UNT Libraries. It has been viewed 602 times , with 13 in the last month . More information about this dissertation can be viewed below.

Who

People and organizations associated with either the creation of this dissertation or its content.

Publisher

Rights Holder

For guidance see Citations, Rights, Re-Use.

  • Hossain, Khalid

Provided By

UNT Libraries

With locations on the Denton campus of the University of North Texas and one in Dallas, UNT Libraries serves the school and the community by providing access to physical and online collections; The Portal to Texas History and UNT Digital Libraries; academic research, and much, much more.

Contact Us

What

Descriptive information to help identify this dissertation. Follow the links below to find similar items on the Digital Library.

Degree Information

Description

A unique process of fabricating a strained layer GexSi1-x on insulator is demonstrated. Such strained heterostructures are useful in the fabrication of high-mobility transistors. This technique incorporates well-established silicon processing technology e.g., ion implantation and thermal oxidation. A dilute GeSi layer is initially formed by implanting Ge+ into a silicon-on-insulator (SOI) substrate. Thermal oxidation segregates the Ge at the growing oxide interface to form a distinct GexSi1-x thin-film with a composition that can be tailored by controlling the oxidation parameters (e.g. temperature and oxidation ambient). In addition, the film thickness can be controlled by implantation fluence, which is important since the film forms pseudomorphically below 2×1016 Ge/cm2. Continued oxidation consumes the underlying Si leaving the strained GeSi film encapsulated by the two oxide layers, i.e. the top thermal oxide and the buried oxide. Removal of the thermal oxide by a dilute HF etch completes the process. Strain relaxation can be achieved by either of two methods. One involves vacancy injection by ion implantation to introduce sufficient open-volume within the film to compensate for the compressive strain. The other depends upon the formation of GeO2. If Ge is oxidized in the absence of Si, it evaporates as GeO(g) resulting in spontaneous relaxation within the strained film. Conditions under which this occurs have been discussed along with elaborated results of oxidation kinetics of Ge-ion implanted silicon. Rutherford backscattering spectrometry (RBS), ion channeling, Raman spectroscopy and scanning electron microscopy (SEM) were used as the characterization techniques.

Subjects

Keyword

Library of Congress Subject Headings

Language

Identifier

Unique identifying numbers for this dissertation in the Digital Library or other systems.

Collections

This dissertation is part of the following collection of related materials.

UNT Theses and Dissertations

Theses and dissertations represent a wealth of scholarly and artistic content created by masters and doctoral students in the degree-seeking process. Some ETDs in this collection are restricted to use by the UNT community.

What responsibilities do I have when using this dissertation?

When

Dates and time periods associated with this dissertation.

Creation Date

  • December 2007

Added to The UNT Digital Library

  • May 2, 2008, 3:14 p.m.

Description Last Updated

  • Dec. 4, 2013, 10:45 a.m.

Usage Statistics

When was this dissertation last used?

Yesterday: 0
Past 30 days: 13
Total Uses: 602

Interact With This Dissertation

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

Citations, Rights, Re-Use

Hossain, Khalid. A Novel Process for GeSi Thin Film Synthesis, dissertation, December 2007; Denton, Texas. (digital.library.unt.edu/ark:/67531/metadc5167/: accessed September 25, 2017), University of North Texas Libraries, Digital Library, digital.library.unt.edu; .