High-Temperature Corrosion of Aluminum Alloys: Oxide-Alloy Interactions and Sulfur Interface Chemistry

PDF Version Also Available for Download.

Description

The spallation of aluminum, chromium, and iron oxide scales is a chronic problem that critically impacts technological applications like aerospace, power plant operation, catalysis, petrochemical industry, and the fabrication of composite materials. The presence of interfacial impurities, mainly sulfur, has been reported to accelerate spallation, thereby promoting the high-temperature corrosion of metals and alloys. The precise mechanism for sulfur-induced destruction of oxides, however, is ambiguous. The objective of the present research is to elucidate the microscopic mechanism for the high-temperature corrosion of aluminum alloys in the presence of sulfur. Auger electron spectroscopy (AES), low energy electron diffraction (LEED), and scanning ... continued below

Creation Information

Addepalli, Swarnagowri December 2000.

Context

This dissertation is part of the collection entitled: UNT Theses and Dissertations and was provided by UNT Libraries to Digital Library, a digital repository hosted by the UNT Libraries. It has been viewed 3897 times , with 22 in the last month . More information about this dissertation can be viewed below.

Who

People and organizations associated with either the creation of this dissertation or its content.

Publisher

Rights Holder

For guidance see Citations, Rights, Re-Use.

  • Addepalli, Swarnagowri

Provided By

UNT Libraries

With locations on the Denton campus of the University of North Texas and one in Dallas, UNT Libraries serves the school and the community by providing access to physical and online collections; The Portal to Texas History and UNT Digital Libraries; academic research, and much, much more.

Contact Us

What

Descriptive information to help identify this dissertation. Follow the links below to find similar items on the Digital Library.

Description

The spallation of aluminum, chromium, and iron oxide scales is a chronic problem that critically impacts technological applications like aerospace, power plant operation, catalysis, petrochemical industry, and the fabrication of composite materials. The presence of interfacial impurities, mainly sulfur, has been reported to accelerate spallation, thereby promoting the high-temperature corrosion of metals and alloys. The precise mechanism for sulfur-induced destruction of oxides, however, is ambiguous. The objective of the present research is to elucidate the microscopic mechanism for the high-temperature corrosion of aluminum alloys in the presence of sulfur. Auger electron spectroscopy (AES), low energy electron diffraction (LEED), and scanning tunneling microscopy (STM) studies were conducted under ultrahigh vacuum (UHV) conditions on oxidized sulfur-free and sulfur-modified Al/Fe and Ni3Al(111). Evaporative deposition of aluminum onto a sulfur-covered iron surface results in the insertion of aluminum between the sulfur adlayer and the substrate, producing an Fe-Al-S interface. Aluminum oxidation at 300 K is retarded in the presence of sulfur. Oxide destabilization, and the formation of metallic aluminum are observed at temperatures > 600 K when sulfur is located at the Al2O3-Fe interface, while the sulfur-free interface is stable up to 900 K. In contrast, the thermal stability (up to at least 1100 K) of the Al2O3 formed on an Ni3Al(111) surface is unaffected by sulfur. Sulfur remains at the oxide-Ni3Al(111) interface after oxidation at 300 K. During annealing, aluminum segregation to the g ¢ -Al2O3-Ni3Al(111) interface occurs, coincident with the removal of sulfur from the interfacial region. A comparison of the results observed for the Al2O3/Fe and Al2O3/Ni3Al systems indicates that the high-temperature stability of Al2O3 films on aluminum alloys is connected with the concentration of aluminum in the alloy.

Language

Identifier

Unique identifying numbers for this dissertation in the Digital Library or other systems.

Collections

This dissertation is part of the following collection of related materials.

UNT Theses and Dissertations

Theses and dissertations represent a wealth of scholarly and artistic content created by masters and doctoral students in the degree-seeking process. Some ETDs in this collection are restricted to use by the UNT community.

What responsibilities do I have when using this dissertation?

When

Dates and time periods associated with this dissertation.

Creation Date

  • December 2000

Added to The UNT Digital Library

  • Sept. 25, 2007, 9:20 p.m.

Description Last Updated

  • May 6, 2016, 6:20 p.m.

Usage Statistics

When was this dissertation last used?

Yesterday: 6
Past 30 days: 22
Total Uses: 3,897

Interact With This Dissertation

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

Citations, Rights, Re-Use

Addepalli, Swarnagowri. High-Temperature Corrosion of Aluminum Alloys: Oxide-Alloy Interactions and Sulfur Interface Chemistry, dissertation, December 2000; Denton, Texas. (digital.library.unt.edu/ark:/67531/metadc2739/: accessed January 17, 2018), University of North Texas Libraries, Digital Library, digital.library.unt.edu; .