Corrosion Protection of Low Carbon Steel By Cation Substituted Magnetite

PDF Version Also Available for Download.

Description

Surfaces of low carbon steel sheet were modified by exposure to highly caustic aqueous solutions containing either chromium or aluminum cations. Corrosion resistances of such surfaces were compared with that of steel surfaces exposed to plain caustic aqueous solution. In all cases a highly uniform, black coating having a spinel structure similar to magnetite (Fe3O4) was obtained. The coated steel surfaces were characterized using X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and Fourier transform infrared spectrophotometry (FTIR). Polarization resistances (Rp) of modified steel surfaces were measured and compared with that of bare steel surfaces. Results ... continued below

Creation Information

Phadnis, Ameya May 2013.

Context

This thesis is part of the collection entitled: UNT Theses and Dissertations and was provided by UNT Libraries to Digital Library, a digital repository hosted by the UNT Libraries. It has been viewed 1381 times , with 21 in the last month . More information about this thesis can be viewed below.

Who

People and organizations associated with either the creation of this thesis or its content.

Chair

Committee Members

Publisher

Rights Holder

For guidance see Citations, Rights, Re-Use.

  • Phadnis, Ameya

Provided By

UNT Libraries

The UNT Libraries serve the university and community by providing access to physical and online collections, fostering information literacy, supporting academic research, and much, much more.

Contact Us

What

Descriptive information to help identify this thesis. Follow the links below to find similar items on the Digital Library.

Degree Information

Description

Surfaces of low carbon steel sheet were modified by exposure to highly caustic aqueous solutions containing either chromium or aluminum cations. Corrosion resistances of such surfaces were compared with that of steel surfaces exposed to plain caustic aqueous solution. In all cases a highly uniform, black coating having a spinel structure similar to magnetite (Fe3O4) was obtained. The coated steel surfaces were characterized using X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and Fourier transform infrared spectrophotometry (FTIR). Polarization resistances (Rp) of modified steel surfaces were measured and compared with that of bare steel surfaces. Results indicate that chromium (Fe2+ Fe3+x Cr3+1-x) or aluminum (Fe2+ Fe3+x Al3+1-x) substituted spinel phases formed on steel surfaces showed higher Rp values compared to only magnetite (Fe2+ 2Fe3+O4) phase formed in the absence of either chromium or aluminum cations. Average Rp values for steel surfaces with chromium containing spinel phase were much higher (21.8 k?) as compared to 1.7 k? for bare steel surfaces. Steel surfaces with aluminum containing spinel phase and steels with plain magnetite coated samples showed average Rp values of 3.3 k? and 2.5 k? respectively. XPS and EDS analysis confirmed presence of cations of chromium and aluminum in Fe3O4 in cation substituted samples. FTIR results showed all coating phases were of spinel form with major absorption bands centered at either 570 cm-1 or 600 cm-1 assigned to Fe3O4 and ?-Fe2O3 respectively.

Subjects

Language

Collections

This thesis is part of the following collection of related materials.

UNT Theses and Dissertations

Theses and dissertations represent a wealth of scholarly and artistic content created by masters and doctoral students in the degree-seeking process. Some ETDs in this collection are restricted to use by the UNT community.

What responsibilities do I have when using this thesis?

When

Dates and time periods associated with this thesis.

Creation Date

  • May 2013

Added to The UNT Digital Library

  • Feb. 1, 2014, 6:14 p.m.

Description Last Updated

  • Nov. 16, 2016, 4:05 p.m.

Usage Statistics

When was this thesis last used?

Yesterday: 0
Past 30 days: 21
Total Uses: 1,381

Interact With This Thesis

Here are some suggestions for what to do next.

Start Reading

PDF Version Also Available for Download.

International Image Interoperability Framework

IIF Logo

We support the IIIF Presentation API

Phadnis, Ameya. Corrosion Protection of Low Carbon Steel By Cation Substituted Magnetite, thesis, May 2013; Denton, Texas. (digital.library.unt.edu/ark:/67531/metadc271878/: accessed October 18, 2018), University of North Texas Libraries, Digital Library, digital.library.unt.edu; .