A year long study has been made of the effect of fatigue on the bond between two epoxy encapsulant formulations and a fused alumina disc. The variables studied included isothermal aging at temperatures up to and including the cure temperature and cyclic thermal aging from +74 to -54/sup 0/C. The encapsulants were glass microballoon filled epoxies differing only in curing agents. One was cured with an aromatic amine eutectic (Shell Curing Agent Z). The other was cured with diethanolamine. The Z cured encapsulant bond failed completely at the bond interface with little or no aging; infrared evidence indicated a soluble ...
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this article.
Follow the links below to find similar items on the Digital Library.
Description
A year long study has been made of the effect of fatigue on the bond between two epoxy encapsulant formulations and a fused alumina disc. The variables studied included isothermal aging at temperatures up to and including the cure temperature and cyclic thermal aging from +74 to -54/sup 0/C. The encapsulants were glass microballoon filled epoxies differing only in curing agents. One was cured with an aromatic amine eutectic (Shell Curing Agent Z). The other was cured with diethanolamine. The Z cured encapsulant bond failed completely at the bond interface with little or no aging; infrared evidence indicated a soluble interlayer as a possible cause of failure. The diethanolamine cured encapsulant survived a year of isothermal aging with little or no evidence of bond degradation. Cyclic thermal aging resulted in gradual bond failure with time. An extrapolation of the cyclic aging data indicates that the stresses induced by thermal cycling would result in complete bond failure in about 1200 days.
This article is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
DeLollis, N.J.Fatigue aging of adhesive bonds,
article,
January 1, 1979;
United States.
(digital.library.unt.edu/ark:/67531/metadc1112775/:
accessed November 18, 2018),
University of North Texas Libraries, Digital Library, digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.