Recovery of deformed and hydrogen-charge palladium
PDF Version Also Available for Download.
Description
Positron lifetime and Doppler-broadening studies made at 300 K have been used to investigate the interaction between interstitial hydrogen and lattice defects in deformed Pd. Specimens were charged with hydrogen at 300 K to levels up to 0.1%. The presence of hydrogen was found to have no effect on the recovery curves of Pd upon annealing to 400/sup 0/C. By 400/sup 0/C the values for both lifetime and Doppler-broadening for both cold worked and cold worked plus hydrogen were below the values obtained for annealed pure Pd. This can be interpreted as gaseous-impurity-trapped vacancies being present after the 1200/sup 0/C …
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this article.
Follow the links below to find similar items on the Digital Library.
Description
Positron lifetime and Doppler-broadening studies made at 300 K have been used to investigate the interaction between interstitial hydrogen and lattice defects in deformed Pd. Specimens were charged with hydrogen at 300 K to levels up to 0.1%. The presence of hydrogen was found to have no effect on the recovery curves of Pd upon annealing to 400/sup 0/C. By 400/sup 0/C the values for both lifetime and Doppler-broadening for both cold worked and cold worked plus hydrogen were below the values obtained for annealed pure Pd. This can be interpreted as gaseous-impurity-trapped vacancies being present after the 1200/sup 0/C anneal, but being swept away by the dislocation microstructure recovery between 200 to 400/sup 0/C.
This article is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
Snead, C. L. Jr.; Lynn, K. G. & Lynch, J. F.Recovery of deformed and hydrogen-charge palladium,
article,
January 1, 1982;
Upton, New York.
(https://digital.library.unt.edu/ark:/67531/metadc1055732/:
accessed March 21, 2025),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.