At a velocity of 2300 cm/min, some improvement began to occur, and at a gas flow
velocity between 2400 and 2550 cm/min, a mixture of large and small equiaxed grains were
produced as shown in Figure 16.
Figure 16. Microstructure Resulting from Gas Flow Plating Velocities
Varying from 2300-2550 cm/min
Here’s what’s next.
This report can be searched. Note: Results may vary based on the legibility of text within the document.
Tools / Downloads
Get a copy of this page or view the extracted text.
Citing and Sharing
Basic information for referencing this web page. We also provide extended guidance on usage rights, references, copying or embedding.
Reference the current page of this Report.
Blay, J.S. Chemical vapor deposition of thoriated tungsten protective cups, report, January 1, 1968; Pittsburgh, Pennsylvania. (https://digital.library.unt.edu/ark:/67531/metadc1026564/m1/35/: accessed March 22, 2019), University of North Texas Libraries, Digital Library, https://digital.library.unt.edu; crediting UNT Libraries Government Documents Department.