A method has been developed for the uniform coating of graphite tubes with carbides of niobium, tantalum, and zirconinm by thermal decomposition of their respective halide vapors. Conditions of coating temperature and pressure are so chosen as to prevent the deposition of metal, but to permit the formation of the carbide as rapidly as carbon can diffuse to the surface. If the carbon diffusion can be made the rate-limiting step, the coating process becomes self- regulating and uniform thickness results. The limits of the temperature-pressure range have been determined experimentally for the thermal decomposition of zirconium iodide and of the …
continued below
Serving as both a federal and a state depository library, the UNT Libraries Government Documents Department maintains millions of items in a variety of formats. The department is a member of the FDLP Content Partnerships Program and an Affiliated Archive of the National Archives.
Descriptive information to help identify this report.
Follow the links below to find similar items on the Digital Library.
Description
A method has been developed for the uniform coating of graphite tubes with carbides of niobium, tantalum, and zirconinm by thermal decomposition of their respective halide vapors. Conditions of coating temperature and pressure are so chosen as to prevent the deposition of metal, but to permit the formation of the carbide as rapidly as carbon can diffuse to the surface. If the carbon diffusion can be made the rate-limiting step, the coating process becomes self- regulating and uniform thickness results. The limits of the temperature-pressure range have been determined experimentally for the thermal decomposition of zirconium iodide and of the chlorides and bromides of niobium, tantalum, and zirconium. With the successful development of coating equipment and definition of conditions, 99 blowpope test specimens were coated with uniform, continuous, and adherent layers of the carbides in three ranges of thickness, light (0.001 in.), medium (0.005 in.), and heavy (0.01 in.). Determinatlons were made of the coefficient for the diffusion of carbon in zirconium carbide as a function of temperature. Exploratory work on small specimens of graphite impregnated with 7 wt.% uranium indicated that the coating results were essentially unchanged, but that loss of uranium occurred. Means of avoiding the loss of uraninm are discussed. (auth)
This report is part of the following collection of related materials.
Office of Scientific & Technical Information Technical Reports
Reports, articles and other documents harvested from the Office of Scientific and Technical Information.
Office of Scientific and Technical Information (OSTI) is the Department of Energy (DOE) office that collects, preserves, and disseminates DOE-sponsored research and development (R&D) results that are the outcomes of R&D projects or other funded activities at DOE labs and facilities nationwide and grantees at universities and other institutions.
Blocher, J.M. Jr.; Ish, C.J.; Leiter, D.P.; Plock, L.F. & Campbell, I.E.Carbide Coatings on Graphite,
report,
June 28, 1957;
Columbus, Ohio.
(https://digital.library.unt.edu/ark:/67531/metadc1021162/:
accessed April 29, 2025),
University of North Texas Libraries, UNT Digital Library, https://digital.library.unt.edu;
crediting UNT Libraries Government Documents Department.