Characterization of boron nitride thin films on silicon (100) wafer.

Characterization of boron nitride thin films on silicon (100) wafer.

Date: August 2007
Creator: Maranon, Walter
Description: Cubic boron nitride (cBN) thin films offer attractive mechanical and electrical properties. The synthesis of cBN films have been deposited using both physical and chemical vapor deposition methods, which generate internal residual, stresses that result in delamination of the film from substrates. Boron nitride films were deposited using electron beam evaporation without bias voltage and nitrogen bombardment (to reduce stresses) were characterize using FTIR, XRD, SEM, EDS, TEM, and AFM techniques. In addition, a pin-on-disk tribological test was used to measure coefficient of friction. Results indicated that samples deposited at 400°C contained higher cubic phase of BN compared to those films deposited at room temperature. A BN film containing cubic phase deposited at 400°C for 2 hours showed 0.1 friction coefficient.
Contributing Partner: UNT Libraries
A Computer-Based Process Control System for a Target Station in a LINAC Facility

A Computer-Based Process Control System for a Target Station in a LINAC Facility

Date: May 1999
Creator: Al-Shantaf, Abdulraouf O.
Description: An event-driven, sequential, process control system was designed for International Isotopes, Inc., to automate and remotely control a target station at the company's linear accelerator facility. The designed system consisted of two major sections: a software program (virtual instrument), which was developed by LabVIEW, and a hardware interface (FieldPoint Modular Distributed I/O System by National Instrument), which had to be a pre-developed system that did not require customization. The designed virtual instrument was tested on a simulation model that mimed the target station. The result was a valid design.
Contributing Partner: UNT Libraries
Computer virus spread containment using feedback control.

Computer virus spread containment using feedback control.

Date: December 2004
Creator: Yelimeli Guruprasad, Arun
Description: In this research, a security architecture based on the feedback control theory has been proposed. The first loop has been designed, developed and tested. The architecture proposes a feedback model with many controllers located at different stages of network. The controller at each stage gives feedback to the one at higher level and a decision about network security is taken. The first loop implemented in this thesis detects one important anomaly of virus attack, rate of outgoing connection. Though there are other anomalies of a virus attack, rate of outgoing connection is an important one to contain the spread. Based on the feedback model, this symptom is fed back and a state model using queuing theory is developed to delay the connections and slow down the rate of outgoing connections. Upon implementation of this model, whenever an infected machine tries to make connections at a speed not considered safe, the controller kicks in and sends those connections to a delay queue. Because of delaying connections, rate of outgoing connections decrease. Also because of delaying, many connections timeout and get dropped, reducing the spread. PID controller is implemented to decide the number of connections going to safe or suspected queue. Multiple ...
Contributing Partner: UNT Libraries
Cost savings realized through proper sizing of an excessive instrument air system.

Cost savings realized through proper sizing of an excessive instrument air system.

Date: December 2003
Creator: Condron, Ewell D.
Description: The purpose of this research was to determine if installing a smaller air compressor could reduce the electrical usage of a large semiconductor manufacturing plant. A 200 horsepower Atlas Copco compressor was installed with the existing 500 horsepower Ingersoll-Rand compressors. Testing was conducted during the regular manufacturing process at MEMC Southwest in Sherman, Texas. Analysis of the data found that installing the new compressor could reduce electrical consumption. The study also found there are specific operational setpoints that allow the compressor to operate more efficiently.
Contributing Partner: UNT Libraries
Design of a Monitoring System for a Plasma Cleaning Machine

Design of a Monitoring System for a Plasma Cleaning Machine

Date: May 1999
Creator: Fooks, Terry M. (Terry Max)
Description: Plasma cleaning is the most effective dry process to remove surface contaminates from a SAW (Surface Acoustical Wave) device. Consistent gas pressures, flows, and good electrical connections between the chamber shelves are necessary for the process to function predictably. In addition, operation of the monitoring system must be transparent to the plasma cleaning unit. This thesis describes a simple solution to the complex problem of monitoring a plasma cleaning system. The monitoring system uses the LabVIEW® G programming language and hardware, both products of National Instruments, Inc.®, to monitor critical parameters necessary to achieve a consistent process when cleaning these devices.
Contributing Partner: UNT Libraries
Determination of the shelf life of aluminum electrolytic capacitors.

Determination of the shelf life of aluminum electrolytic capacitors.

Date: May 2002
Creator: Wynne, Edward McFaddin
Description: The aluminum electrolytic capacitor is used extensively in the electric utility industry. A factor limiting the storage of spare capacitors is the integrity of the aluminum oxide dielectric, which over time breaks down contributing to a shelf life currently estimated at one nuclear power electric generating station to be approximately five years. This project examined the electrical characteristics of naturally aged capacitors of several different styles to determine if design parameters were still within limits. Additionally, the effectiveness of a technique known as “Reforming” was examined to determine its impact on those characteristics.
Contributing Partner: UNT Libraries
Development of a Simplified Fracture Toughness Tool for Polymers

Development of a Simplified Fracture Toughness Tool for Polymers

Date: August 1997
Creator: Marnock, Patrick J. (Patrick Joseph)
Description: This thesis presents research toward the development of a simple inexpensive fracture toughness tool for polymeric materials. Experiments were conducted to test the specimen configuration and the fracture toughness tool against an established ASTM standard for polymer fracture toughness, D5045, and a commonly used four-point bend method. The materials used in this study were polycarbonate and high density polyethylene. Reductions in both the production time and the variability resulting from the preparation of the specimens were addressed through the use of specially designed fixtures. The effects from the razor cut depths used in the chevron notch were compared to the fracture toughness values obtained in order to determine the effect upon the validity of the fracture toughness.
Contributing Partner: UNT Libraries
Effect of Amines as Corrosion Inhibitors for a Low Carbon Steel in Power Industry

Effect of Amines as Corrosion Inhibitors for a Low Carbon Steel in Power Industry

Date: December 2004
Creator: Díaz, Jorge G.
Description: Commonly used amines in power industry, including morpholine, DBU (1,8-diazabicyclo[5.4.0]undec-7-ene), and DMA (dimethylallylamine) were evaluated for their effect on AISI 1018 steel at 250oF. Samples were exposed to an autoclave containing amine added aqueous solution at pH of 9.5 for 1, 2, 4, 6, 8, and 12 hours. Morphology studies were carried using scanning electron microscope (SEM), phase analysis was done utilizing Fourier transform infrared spectroscopy (FTIR), and weight loss was performed to assess kinetics of oxidation. Control samples showed the highest metal dissolution rate. DBU showed the best performance in metal protection and SEM indicated the presence of a free-crack layer formed by fine particles in that set. FTIR showed that DBU apparently favored the formation of magnetite. It is believed that fine particles impede intrusion of aggressive ions into the metal surface by forming a barrier layer. FTIR demonstrated that DMA formed more oxyhydroxides, whereas morpholine presented magnetite to hematite transformation as early as 2 hours. SEM revealed that control and DMA produced acicular particles characteristic of oxyhydroxides while morpholine and DBU presented more equiaxed particles.
Contributing Partner: UNT Libraries
Effects of a surface engineered metallic coating on elastomeric valve stem seal leakage

Effects of a surface engineered metallic coating on elastomeric valve stem seal leakage

Date: December 2000
Creator: Taylor, John Abner
Description: Valve stem seal leakage is a major source of fugitive emissions, and controlling these emissions can result in added expense in leak detection and repair programs. Elastomeric O-rings can be used as valve stem seals, and O-ring manufacturers recommend lubrication of elastomeric seals to prevent damage and to assure proper sealing. In this research, a metallic coating was applied as a lubricant using a vacuum vapor deposition process to the surface of elastomeric valve stem seals. Valve stem leak measurements were taken to determine if the coated O-rings, alone or with the recommended lubrication, reduced valve stem seal leakage. This research determined that the metallic coating did not reduce valve stem leakage.
Contributing Partner: UNT Libraries
FEM of nanoindentation on micro- and nanocrystalline Ni: Analysis of factors affecting hardness and modulus values.

FEM of nanoindentation on micro- and nanocrystalline Ni: Analysis of factors affecting hardness and modulus values.

Date: August 2005
Creator: Pothapragada, Raja Mahesh
Description: Nanoindentation is a widely used technique to measure the mechanical properties of films with thickness ranging from nanometers to micrometers. A much better understanding of the contact mechanics is obtained mostly through finite element modeling. The experiments were modeled using the software package Nano SP1 that is based on COSMOSM™ (Structural Research & Analysis Corp, www.cosmosm.com), a finite element code. The fundamental material properties affecting pile-up are the ratio of the effective modulus to yield stress Eeff/σ and the work hardening behavior. Two separate cases of work hardening rates were considered; one with no work hardening rate and other with a linear work hardening rate. Specifically, it is observed that pile up is large only when hf/hmax is close to one and degree of work hardening rate is small. It should also be noted that when hf/hmax < 0.7 very little pile-up is observed no matter what the work-hardening behavior of the material. When pile-up occurs the contact area is greater than that predicted by the experimental methods and both the hardness and modulus are overestimated. In this report the amount by which these properties are overestimated are studied and got to be around 22% approx. Bluntness of the tip ...
Contributing Partner: UNT Libraries