Analysis of Thermoplastic Polyimide + Polymer Liquid Crystal Blends

Analysis of Thermoplastic Polyimide + Polymer Liquid Crystal Blends

Date: May 1998
Creator: Gopalanarayanan, Bhaskar
Description: Thermoplastic polyimides (TPIs) exhibit high glass transition temperatures (Tgs), which make them useful in high performance applications. Amorphous and semicrystalline TPIs show sub-Tg relaxations, which can aid in improving strength characteristics through energy absorption. The a relaxation of both types of TPIs indicates a cooperative nature. The semicrystalline TPI shows thermo-irreversible cold crystallization phenomenon. The polymer liquid crystal (PLC) used in the blends is thermotropic and with longitudinal molecular structure. The small heat capacity change (ACP) associated with the glass transition indicates the PLC to be rigid rod in nature. The PLC shows a small endotherm associated with the melting. The addition of PLC to the semicrystalline TPI does not significantly affect the Tg or the melting point (Tm). The cold crystallization temperature (Tc) increases with the addition of the PLC, indicating channeling phenomenon. The addition of PLC also causes a negative deviation of the ACP, which is another evidence for channeling. The TPI, PLC and their blends show high thermal stability. The semicrystalline TPI absorbs moisture; this effect decreases with the addition of the PLC. The absorbed moisture does not show any effect on the degradation. The addition of PLC beyond 30 wt.% does not result in an improvement ...
Contributing Partner: UNT Libraries
Characterization of cure kinetics and physical properties of a high performance, glass fiber-reinforced epoxy prepreg and a novel fluorine-modified, amine-cured commercial epoxy.

Characterization of cure kinetics and physical properties of a high performance, glass fiber-reinforced epoxy prepreg and a novel fluorine-modified, amine-cured commercial epoxy.

Date: December 2003
Creator: Bilyeu, Bryan
Description: Kinetic equation parameters for the curing reaction of a commercial glass fiber reinforced high performance epoxy prepreg composed of the tetrafunctional epoxy tetraglycidyl 4,4-diaminodiphenyl methane (TGDDM), the tetrafunctional amine curing agent 4,4'-diaminodiphenylsulfone (DDS) and an ionic initiator/accelerator, are determined by various thermal analysis techniques and the results compared. The reaction is monitored by heat generated determined by differential scanning calorimetry (DSC) and by high speed DSC when the reaction rate is high. The changes in physical properties indicating increasing conversion are followed by shifts in glass transition temperature determined by DSC, temperature-modulated DSC (TMDSC), step scan DSC and high speed DSC, thermomechanical (TMA) and dynamic mechanical (DMA) analysis and thermally stimulated depolarization (TSD). Changes in viscosity, also indicative of degree of conversion, are monitored by DMA. Thermal stability as a function of degree of cure is monitored by thermogravimetric analysis (TGA). The parameters of the general kinetic equations, including activation energy and rate constant, are explained and used to compare results of various techniques. The utilities of the kinetic descriptions are demonstrated in the construction of a useful time-temperature-transformation (TTT) diagram and a continuous heating transformation (CHT) diagram for rapid determination of processing parameters in the processing of prepregs. Shrinkage ...
Contributing Partner: UNT Libraries
Charge interaction effects in epoxy with cation exchanged montmorillonite clay and carbon nanotubes.

Charge interaction effects in epoxy with cation exchanged montmorillonite clay and carbon nanotubes.

Date: May 2005
Creator: Butzloff, Peter Robert
Description: The influence of charge heterogeneity in nanoparticles such as montmorillonite layered silicates (MLS) and hybrid systems of MLS + carbon nanotubes was investigated in cured and uncured epoxy. Epoxy nanocomposites made with cation-exchanged montmorillonite clay were found to form agglomerates near a critical concentration. Using differential scanning calorimetry it was determined that the mixing temperature of the epoxy + MLS mixture prior to the addition of the curing agent critically influenced the formation of the agglomerate. Cured epoxy samples showed evidence of the agglomerate being residual charge driven by maxima and minima in the concentration profiles of thermal conductivity and dielectric permittivity respectively. A hybrid nanocomposite of MLS and aniline functionalized multi walled nanotubes indicated no agglomerates. The influence of environmentally and process driven properties on the nanocomposites was investigated by examination of moisture, ultrasound, microwaves and mechanical fatigue on the properties of the hybrid systems. The results point to the importance of charge screening by adsorbed or reacted water and on nanoparticulates.
Contributing Partner: UNT Libraries
Deposition and characterization of pentacene film.

Deposition and characterization of pentacene film.

Date: December 2003
Creator: Singh, Nidhi
Description: Many organic materials have been studied to be used as semiconductors, few of them being pentacene and polythiophene. Organic semiconductors have been investigated to make organic thin film transistors. Pentacene has been used in the active region of the transistors. Transistors fabricated with pentacene do not have very high mobility. But in some applications, high mobility is not needed. In such application other properties of organic transistors are used, such as, ease of production and flexibility. Organic thin film transistors (OTFT) can find use as low density storage devices, such as smart cards or I.D. tags, and displays. OTFT are compatible with polymeric substrates and hence can find use as flexible computer screens. This project aims at making 'smart clothes', the cheap way, with pentacene based OTFT. This problem in lieu of thesis describes a way to deposit pentacene films and characterize it. Pentacene films were deposited on substrates and characterized using x-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). The substrate used was ~1500Å platinum on silicon wafer or bare silicon wafer. was used. A deposition system for vacuum deposition of pentacene was assembled. The XRD data for deposited pentacene films shows the presence of two phases, single ...
Contributing Partner: UNT Libraries
The Electron Emission Characteristics of Aluminum, Molybdenum and Carbon Nanotubes Studied by Field Emission and Photoemission.

The Electron Emission Characteristics of Aluminum, Molybdenum and Carbon Nanotubes Studied by Field Emission and Photoemission.

Date: December 2002
Creator: Sosa, Edward Delarosa
Description: The electron emission characteristics of aluminum, molybdenum and carbon nanotubes were studied. The experiments were setup to study the emission behavior as a function of temperature and exposure to oxygen. Changes in the surface work function as a result of thermal annealing were monitored with low energy ultra-violet photoelectron spectroscopy for flat samples while field emission energy distributions were used on tip samples. The change in the field emission from fabricated single tips exposed to oxygen while in operation was measured using simultaneous Fowler-Nordheim plots and electron energy distributions. From the results a mechanism for the degradation in the emission was concluded. Thermal experiments on molybdenum and aluminum showed that these two materials can be reduced at elevated temperatures, while carbon nanotubes on the other hand show effects of oxidation. To purely reduce molybdenum a temperature in excess of 750 ºC is required. This temperature exceeds that allowed by current display device technology. Aluminum on the other hand shows reduction at a much lower temperature of at least 125 ºC; however, its extreme reactivity towards oxygen containing species produces re-oxidation. It is believed that this reduction is due to the outward diffusion of aluminum atoms through the oxide. Carbon nanotubes ...
Contributing Partner: UNT Libraries
Epoxy + liquid crystalline epoxy coreacted networks

Epoxy + liquid crystalline epoxy coreacted networks

Date: December 2000
Creator: Punchaipetch, Prakaipetch
Description: Molecular reinforcement through in-situ polymerization of liquid crystalline epoxies (LCEs) and a non-liquid crystalline epoxy has been investigated. Three LCEs: diglycidyl ether of 4,4'-dihydroxybiphenol (DGE-DHBP) and digylcidyl ether of 4-hydroxyphenyl-4"-hydroxybiphenyl-4'-carboxylate (DGE-HHC), were synthesized and blended with diglycidyl ether of bisphenol F (DGEBP-F) and subsequently cured with anhydride and amine curing agents. Curing kinetics were determined using differential scanning calorimetry (DSC). Parameters for autocatalytic curing kinetics of both pure monomers and blended systems were determined. The extent of cure for both monomers was monitored by using Fourier transform infrared spectroscopy (FT-IR). The glass transitions were evaluated as a function of composition using DSC and dynamic mechanical analysis (DMA). The results show that the LC constituent affects the curing kinetics of the epoxy resin and that the systems are highly miscible. The effects of molecular reinforcement of DGEBP-F by DGE-DHBP and DGE-HHC were investigated. The concentration of the liquid crystalline moiety affects mechanical properties. Tensile, impact and fracture toughness tests results are evaluated. Scanning electron microscopy of the fracture surfaces shows changes in failure mechanisms compared to the pure components. Results indicate that mechanical properties of the blended samples are improved already at low concentration by weight of the LCE added into ...
Contributing Partner: UNT Libraries
Hypotheses for Scratch Behavior of Polymer Systems that Recover

Hypotheses for Scratch Behavior of Polymer Systems that Recover

Date: May 2002
Creator: Bujard, Bernard
Description: Scratch recovery is a desirable property of many polymer systems. The reason why some materials have demonstrated excellent scratch recovery while others do not has been a mystery. Explaining the scratch resistance based upon the hardness of a material or its crosslink density is incorrect. In this thesis, novel polymers were tested in an attempt to discover materials that show excellent scratch recovery - one of the most important parameters in determining the wear of a material. Several hypotheses were developed in an attempt to give an accurate picture of how the chemical structure of a polymer affects its scratch recovery. The results show that high scratch recovery is a complex phenomenon not solely dependent upon the presence of electronegative atoms such as fluorine.
Contributing Partner: UNT Libraries
Influence of design and coatings on the mechanical reliability of semiconductor wafers.

Influence of design and coatings on the mechanical reliability of semiconductor wafers.

Date: August 2002
Creator: Yoder, Karl J.
Description: We investigate some of the mechanical design factors of wafers and the effect on strength. Thin, solid, pre-stressed films are proposed as a means to improve the bulk mechanical properties of a wafer. Three-point bending was used to evaluate the laser scribe density and chemical processing effect on wafer strength. Drop and strike tests were employed to investigate the edge bevel profile effect on the mechanical properties of the wafer. To characterize the effect of thin films on strength, one-micron ceramic films were deposited on wafers using PECVD. Coated samples were prepared by cleaving and were tested using four-point bending. Film adhesion was characterized by notched four-point bending. RBS and FTIR were used to obtain film chemistry, and nanoindentation was used to investigate thin film mechanical properties. A stress measurement gauge characterized residual film stress. Mechanical properties of the wafers correlated to the residual stress in the film.
Contributing Partner: UNT Libraries
Investigation of growth kinetics of self-assembling monolayers by means of contact angle, optical ellipsometry, angle-resolved XPS and IR spectroscopy.

Investigation of growth kinetics of self-assembling monolayers by means of contact angle, optical ellipsometry, angle-resolved XPS and IR spectroscopy.

Date: August 2004
Creator: Jakubowicz, Agnieszka
Description: Absorption of octadecanethiol and p-nitrobenzenethiol onto gold surfaces from ethanol solutions has been studied by means of contact angle, optical ellipsometry, angle-resolved XPS (ARXPS), and with grazing angle total reflection FTIR. Growth of the monolayers from dilute solutions has been monitored and Langmuir isotherm adsorption curves were fitted to experimental data. A saturated film is formed within approximately 5h after immersion in solutions of concentrations ranging from 0.0005mM to 0.01mM. We found, that the final density of monolayer depends on the concentration of the solution.
Contributing Partner: UNT Libraries
Materials properties of hafnium and zirconium silicates: Metal interdiffusion and dopant penetration studies.

Materials properties of hafnium and zirconium silicates: Metal interdiffusion and dopant penetration studies.

Date: August 2002
Creator: Quevedo-Lopez, Manuel Angel
Description: Hafnium and Zirconium based gate dielectrics are considered potential candidates to replace SiO2 or SiON as the gate dielectric in CMOS processing. Furthermore, the addition of nitrogen into this pseudo-binary alloy has been shown to improve their thermal stability, electrical properties, and reduce dopant penetration. Because CMOS processing requires high temperature anneals (up to 1050 °C), it is important to understand the diffusion properties of any metal associated with the gate dielectric in silicon at these temperatures. In addition, dopant penetration from the doped polysilicon gate into the Si channel at these temperatures must also be studied. Impurity outdiffusion (Hf, Zr) from the dielectric, or dopant (B, As, P) penetration through the dielectric into the channel region would likely result in deleterious effects upon the carrier mobility. In this dissertation extensive thermal stability studies of alternate gate dielectric candidates ZrSixOy and HfSixOy are presented. Dopant penetration studies from doped-polysilicon through HfSixOy and HfSixOyNz are also presented. Rutherford backscattering spectroscopy (RBS), heavy ion RBS (HI-RBS), x-ray photoelectron spectroscopy (XPS), high resolution transmission electron microscopy (HR-TEM), and time of flight and dynamic secondary ion mass spectroscopy (ToF-SIMS, D-SIMS) methods were used to characterize these materials. The dopant diffusivity is calculated by modeling ...
Contributing Partner: UNT Libraries